Solder paste material technology for elimination of high warpage surface mount assembly defects

Abstract

A composition including a solder flux including a rosin material have a property to maintain a less than 10 percent drop in tackiness from an initial tackiness value of 20 gf to 120 gf over a temperature regime of 20° C. to 200° C. A composition including a solder powder; and a solder flux including a rosin material including a softening temperature of 150° C. to 200° C. and a molecular weight of 300 g/mol to 600 g/mol. A method including introducing a solder paste to one or more contact pads of a substrate, the solder paste including a solder powder and a solder flux including a rosin material including a softening temperature of 150° C. to 190° C. and a molecular weight of 300 g/mol to 600 g/mol; contacting the solder paste with a solder ball of a package substrate; and heating the solder paste.