# US 2014/0154476 A1 · Heating Article Comprising a Microstructured Heat-Stable Coating and Method of Manufacturing Such an Article > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 2014/0154476 A1 - Document ID: US20140154476A1 - Status: Published application - Kind: A1 - Application number: 14/234,221 - Filed: 2012-07-25 - Published: 2014-06-05 - Earliest claimed: 2011-07-25 - Assignees: Seb S.A. - Inventors: Jean-Luc Perillon; Stephanie Le Bris - Web page: https://patentgrep.com/patent/US20140154476A1 ## CPC - A47J 36/025: {Vessels with non-stick features, e.g. coatings} - B05D 5/08: to obtain an anti-friction or anti-adhesive surface (rendering particulate materials free-flowing in general, e.g. making them hydrophobic B01J2/30) - B05D 7/542: {the two layers being cured or baked together} - B41M 3/00: Printing processes to produce particular kinds of printed work, e.g. patterns ({printing apparatus or machines of special type or for particular purposes B41F17/00;} special designs or pictures per se B44F; manufacturing printed circuits using printing techniques H05K3/12 {; manufacturing organic semiconductor devices using printing techniques H10K71/13}) - B05D 5/02: to obtain a matt or rough surface - B05D 5/083: {involving the use of fluoropolymers} - B05D 7/52: {Two layers} - Y10T 428/24612: Composite web or sheet - A47J: KITCHEN EQUIPMENT; COFFEE MILLS; SPICE MILLS; APPARATUS FOR MAKING BEVERAGES - B05D: PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL (conveying articles or workpieces through baths of liquid B65G, e.g. B65G49/02) - B41M: PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING, (correction of typographical errors B41J; processes for applying transfer pictures or the like B44C1/16; fluid media for correction of typographical errors by coating C09D10/00; printing textiles D06P) - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract Provided is a heating article comprising a substrate having two opposite surfaces, a heat-stable coating comprising at least one base layer comprising at least one heat-stable binder, said base layer being arranged on one of the surfaces of the substrate, and one microstructured surface layer comprising a heat-stable binder of the same chemical nature as that of the base layer. The microstructured layer partly or fully covers the base layer and is sintered integrally to it. The microstructured surface layer has a relief with patterns comprised of local variations in its surface level, said relief having a regularity in average pitch Ar with a variation SAr which is not more than 10% higher or lower than the value of said average pitch Ar. A method of manufacturing such an article is also provided. ## Claims ### Claim 1 A heating article comprising: a substrate having two opposite sides, a heat-stable coating comprising: at least a base layer comprising at least one heat-stable binder, said base layer being arranged on one of the sides of the substrate, and a microstructured surface layer comprising a heat-stable binder of the same chemical nature as that of the base layer, said microstructured layer partially or completely covering said base layer and being sintered integrally with the latter, said microstructured surface layer having a relief with patterns constituted by local variations in its surface level, said relief having a regularity in average pitch Ar with a variation SAr not more than 10% of the value said average pitch Ar, on either side of this value Ar. ### Claim 2 (depends on 1) The heating article, according to claim 1, wherein said relief exhibits an average surface roughness Ra with a variation SAr of at most 10% of the value of said average depth roughness Ra on both sides of this value Ra. ### Claim 3 (depends on 1) The heating article, according to claim 1, wherein the average pitch Ar of the relief ranges between 5 μm and 75 μm. ### Claim 4 (depends on 2) The heating article, according to claim 2, wherein the average depth roughness Ra of the relief ranges between 5 μm and 50 μm. ### Claim 5 (depends on 1) The heating article, according to claim 1, wherein the heat-stable binder of the base layer and that of the microstructured layer comprise a fluorocarbon resin or a mixture of fluorocarbon resins either alone or mixed with other heat-stable resins. ### Claim 6 (depends on 1) The heating article, according to claim 1, wherein the heat-stable binder of the base layer and that of the microstructured layer are made of a sol-gel material comprising at least one matrix of at least a metallic polyalkoxylate. ### Claim 7 (depends on 5) The heating article, according to claim 5, wherein the microstructured layer is in the form of fluorocarbon compounds forming the relief of the heat-stable coating, said fluorocarbon compounds being sintered integrally with the base layer. ### Claim 8 (depends on 5) The heating article, according to claim 5, wherein the microstructured layer further comprises microparticles each having a size ranging between 5 μm and 10 μm and made of a material having a melting temperature exceeding by at least 20° C. the melting temperature of the heat-stable binders of the base layer and the microstructured layer, said microparticles being regularly arranged on the base layer and being covered by a continuous film of said heat-stable binder of the microstructured layer, said microparticles creating local variations in the surface level of said film. ### Claim 9 (depends on 8) The heating article, according to claim 8, wherein the microparticles have a hardness that is higher than 5 on the Mohs scale. ### Claim 10 (depends on 8) The heating article, according to claim 8, wherein the microparticles are one of aluminum oxide, silica or zirconium particles. ### Claim 11 (depends on 1) The heating article, according to claim 1, wherein the microstructured layer is covered by a finishing layer having a thickness less than the variation SRa of the roughness of the microstructured layer. ### Claim 12 A method of manufacturing a heating article comprising the following steps: a) providing a substrate comprising two opposite sides, then b) producing a heat-stable coating comprising: formation of, on at least one of the sides of the substrate, at least a base layer comprising at least one heat-stable binder, and formation of, on all or part of the base layer), a microstructured layer partially or totally comprising a heat-stable binder of the same nature as that of the base layer, the formation of the microstructured layer comprising inkjet printing by projection at determined positions (PI, P2, . . . , PN) of microdroplets of a dispersion in a solvent of a structuring material, said printing being achieved with a micrometric printing pitch (d), and c) curing the heat-stable coating to sinter the binder of the base layer integrally with the binder of the microstructured layer, such as to solidify the assembly and form a relief with patterns formed by local variations in the surface level of the heat-stable coating. ### Claim 13 (depends on 12) The method according to claim 12, wherein the printing pitch (d) ranges between 5 and 75 μm. ### Claim 14 (depends on 12) The method according to claim 12, wherein the heat-stable binders of the base and microstructured layers comprise a fluorocarbon resin or a mixture of fluorocarbon resins, alone or as a mixture with other heat-stable resins. ### Claim 15 (depends on 14) The method according to claim 14, wherein the structuring material consists entirely of the heat-stable binder of the microstructured layer, the heat-stable binder being present in the dispersion in an amount ranging between 2% to 20% in weight with respect to the total weight of the dispersion. ### Claim 16 (depends on 14) The method according to claim 14, wherein the structuring material comprises microparticles of a material that has a melting temperature that is higher by at least 20° C. to the melting temperature of the heat-stable binders of the base and microstructured layers, dispersed in the solvent in an amount of 2% to 20% in weight with respect to the total weight of the dispersion, and in that the printing of the microdroplets of the dispersion is followed by the formation of a continuous film covering said microparticles, said film comprising the heat-stable binder of the microstructured layer and said microparticles creating local variations of the surface level of said film. ### Claim 17 (depends on 16) The method according to claim 16, wherein the microparticles have a hardness that is higher than 5 on the Mohs scale. ### Claim 18 (depends on 16) The method according to claim 16, wherein the microparticles are one of aluminum oxide, silica or zirconia. ### Claim 19 (depends on 12) The method according to claim 12, wherein the heat-stable binders of the base and the microstructured layers comprise water and at least one sol-gel precursor of metallic alkoxyde type dispersed in an alcoholic medium. ### Claim 20 (depends on 19) The method according to claim 19, wherein the method comprises a drying of the microdroplet or microdroplets projected in each position before the projection of another microdroplet in said position.