Hydrophilic polyester polycarbonate polyols for high temperature diesel applications

Abstract

Embodiments of the invention generally relate to polyols having resistance to hydrocarbons and articles made therefrom. More specifically, embodiments of the invention generally relate to hydrophilic polyester-polycarbonate polyols having resistance to hydrocarbons at high temperatures and articles made therefrom. The novel hydrophilic polyester-polycarbonate polyols described herein may be used in adhesive or elastomer applications requiring enhanced oil and/or diesel resistance. The disclosed polyols are liquid at room temperature, which facilitates processing into polyurethane products As described herein, an elastomer made from such hydrophilic polyester-polycarbonate polyols and methylene diphenyl diisocyanate (MDI) retained >90% of tensile strength after 500 hours ageing at 121 degrees Celsius. A comparative example made from a polyester polyol retained 50% of tensile strength under similar conditions.