US 2014/0004373 A1 · TIN-PLATED COPPER-ALLOY MATERIAL FOR TERMINAL AND METHOD FOR PRODUCING THE SAME

Abstract

Tin-plated copper-alloy material for terminal in which: a CuSn alloy layer/a NiSn alloy layer/a Ni or Ni alloy layer are formed between a Sn-based surface layer and a substrate made of Cu or Cu alloy; the CuSn alloy layer is a compound-alloy layer containing Cu6Sn5 as a major proportion and a part of Cu in the Cu6Sn5 is displaced by Ni; the NiSn alloy layer is a compound-alloy layer containing Ni3Sn4 as a major proportion and a part of Ni in the Ni3Sn4 is displaced by Cu; an average interval S of point peaks of the CuSn alloy layer is not less than 0.8 μm and not more than 2.0 μm; an average thickness of the Sn-based surface layer is not less than 0.2 μm and not more than 0.6 μm; an exposed-area rate of the CuSn alloy layer exposed at a surface of the Sn-based surface layer is not less than 1% and not more than 40%; an average of equivalent-circle diameter of the exposed portions of the CuSn alloy layer exposed at the surface of the Sn-based surface layer is not less than 0.1 μm and not more than 1.5 μm; and dynamic friction coefficient is not more than 0.3.

Claims3

Dependent claims

A tin-plated copper-alloy material for terminal wherein:

a Sn-based surface layer is formed on a surface of a substrate made of Cu or Cu alloy, and a CuSn alloy layer/a NiSn alloy layer/a Ni or Ni alloy layer are formed in sequence from the Sn-based surface layer between the Sn-based surface layer and the substrate, the CuSn alloy layer is a compound-alloy layer containing Cu6Sn5 as a major proportion and a part of Cu in the Cu6Sn5 is displaced by Ni;
the NiSn alloy layer is a compound-alloy layer containing Ni3Sn4 as a major proportion and a part of Ni in the Ni3Sn4 is displaced by Cu;
an average interval S of point peaks of the CuSn alloy layer is not less than 0 8 μm and not more than 2.0 μm;
an average thickness of the Sn-based surface layer is not less than 0.2 μm and not more than 0.6 μm;
an exposed-area rate of the CuSn alloy layer exposed at a surface of the Sn-based surface layer is not less than 1% and not more than 40%;
an average of equivalent-circle diameter of exposed portions of the CuSn alloy layer exposed at the surface of the Sn-based surface layer is not less than 0.1 μm and not more than 1.5 μm;
and
dynamic friction coefficient is not more than 0.3.

5 more elements

A method for producing tin-plated copper alloy material for terminal wherein:

a Ni or Ni alloy layer/a NiSn alloy layer/a CuSn alloy layer/a Sn-based surface layer are formed on a substrate made of Cu or Cu alloy by forming a Ni or Ni alloy plating layer, a Cu plating layer and a Sn plating layer in sequence on the substrate and then operating a reflow treatment,
a thickness of the Ni or Ni alloy plating layer is set in a range of not less than 0.05 μm and not more than 1.0 μm;
a thickness of the Cu plating layer is set in a range of not less than 0.05 μm and not more than 0.20 μm;
a thickness of the Sn plating layer is set in a range of not less than 0.5 μm and not more than 1.0 μm;
and
the reflow treatment is operated by heating the substrate until surface temperature of the substrate is increased to not lower than 240° C. and not higher than 360° C., then rapidly cooling after holding the temperature for a predetermined duration set as below (1) or (2):
(1) if the thickness of the Sn plating layer is in a range of not less than 0.5 μm to less than 0.7 μm:
in a case in which the thickness of the Cu plating layer is in a range of not less than 0.05 to less than 0.16 μm, the predetermined duration is not shorter than 1 second to not more than 6 seconds;
or
in a case in which the thickness of the Cu plating layer is in a range of not less than 0.16 μm to not more than 0.20 μm, the predetermined duration is not shorter than 3 seconds to not more than 9 seconds, or
(2) if the thickness of the Sn plating layer is in a range of not less then 0.7 μm to not more than 1.0 μm:
in the case in which he thickness of the Cu plating layer is in a range of not less than 0.05 to less than 0.16 μm, the predetermined duration is not shorter than 3 second to not more than 9 seconds;
or
in a case in which the thickness of the Cu plating layer is in a range of not less than 0.16 μm to not more than 0.20 μm, the predetermined duration is not shorter than 6 seconds to not more than 12 seconds.

11 more elements

Dependencies are inferred from the claim text.

Tin-plated copper-alloy material for terminal and method for producing the same

Life of this patent

Tin-plated copper-alloy material for terminal and method for producing the same

Life of this patent

Abstract

Claims3