Masterbatch composition
AssigneeDow Global Technologies LLC
InventorsSatish V. Awate, Brad A. Cobler, Rajen M. Patel
Life of this patent
Estimating the term…
Abstract
The instant invention provides a masterbatch composition, method of producing the same, polymeric compositions suitable for films, and films made therefrom. The masterbatch composition according to the present invention comprises: (a) from 70 to 90 percent by weight of a filler comprising calcium carbonate; and (b) from 10 to 30 percent by weight of a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.
Claims6
A masterbatch composition comprising:
- from 70 to 90 percent by weight of a filler comprising calcium carbonate;
- and
- from 10 to 30 percent by weight of a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.
A method for producing a masterbatch composition comprising the steps of:
- selecting a filler comprising calcium carbonate;
- selecting a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.;
- compounding that filler into said propylene/alpha-olefin copolymer composition;
- and
- thereby producing said masterbatch composition, wherein said masterbatch composition comprises from 70 to 90 percent by weight of that filler and from 10 to 30 percent by weight of said propylene/alpha-olefin copolymer composition.
A polymeric composition suitable for films comprising:
- from 10 to 40 percent by weight of a masterbatch composition comprising:
- from 70 to 90 percent by weight of a filler comprising calcium carbonate;
- and
- from 10 to 30 percent by weight of a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.;
- and
- from 60 to 90 percent by weight of a polyethylene composition.
A process for producing a polymeric composition suitable for films comprising the steps of:
- selecting from 10 to 40 percent by weight of a masterbatch composition comprising:
- from 70 to 90 percent by weight of a filler comprising calcium carbonate;
- and
- from 10 to 30 percent by weight of a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.;
- selecting from 60 to 90 percent by weight of a polyethylene composition;
- and
- compounding said mater batch composition into said polyethylene composition;
- thereby producing said polymeric composition suitable for films.
A film comprising:
- a polymeric composition comprising:
- from 10 to 40 percent by weight of a masterbatch composition comprising:
- from 70 to 90 percent by weight of a filler comprising calcium carbonate;
- and
- from 10 to 30 percent by weight of a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.;
- and
- from 60 to 90 percent by weight of a polyethylene composition.
A process for making a film comprising the steps of:
- selecting a polymeric composition comprising:
- from 10 to 40 percent by weight of a masterbatch composition comprising:
- from 70 to 90 percent by weight of a filler comprising calcium carbonate;
- and
- from 10 to 30 percent by weight of a propylene/alpha-olefin copolymer composition, wherein said propylene/alpha-olefin copolymer composition has a crystallinity in the range of from 1 percent by weight to 30 percent by weight, a heat of fusion in the range of from 2 Joules/gram to 50 Joules/gram, and a DSC melting point in the range of 25° C. to 110° C.;
- and
- from 60 to 90 percent by weight of a polyethylene composition;
- and
- forming said polymeric composition into a film via blown film process.
Dependencies are inferred from the claim text.