Abstract
Alloy cast iron for a seal, a seal, and a method of manufacturing the seal are provided. The alloy cast iron for a seal includes 3.8 wt % to 4.2 wt % of carbon, 3.3 wt % to 4.7 wt % of nickel, 2 wt % to 5 wt % of molybdenum, 1.2 wt % to 2.0 wt % of silicon, 16 wt % to 18 wt % of chrome, 0.8 wt % to 1.5 wt % of manganese, and the remaining of iron. Therefore, a seal can be produced using a centrifugal casting method and thus productivity of the seal is improved and the seal having excellent abrasion resistance is produced.
Claims5
A seal comprising 3.8 wt % to 4.2 wt % of carbon, 3.3 wt % to 4.7 wt % of nickel, 2 wt % to 5 wt % of molybdenum, 1.2 wt % to 2.0 wt % of silicon, 16 wt % to 18 wt % of chrome, 0.8 wt % to 1.5 wt % of manganese, and the remaining of iron.
A method of manufacturing a seal, the method comprising:
- melting alloy cast iron for the seal;
- injecting the melted alloy cast iron into a rotation mold;
- forming the seal by a rotation of the rotation mold;
- and
- separating the seal from the rotation mold and performing heat treatment of the seal,
- wherein the alloy cast iron comprises 3.8 wt % to 4.2 wt % of carbon, 3.3 wt % to 4.7 wt % of nickel, 2 wt % to 5 wt % of molybdenum, 1.2 wt % to 2.0 wt % of silicon, 16 wt % to 18 wt % of chrome, 0.8 wt % to 1.5 wt % of manganese, the remaining of iron, and impurities generated upon melting.
Alloy cast iron for a seal comprising 3.8 wt % to 4.2 wt % of carbon, 3.3 wt % to 4.7 wt % of nickel, 2 wt % to 5 wt % of molybdenum, 1.2 wt % to 2.0 wt % of silicon, 16 wt % to 18 wt % of chrome, 0.8 wt % to 1.5 wt % of manganese, and the remaining of iron.