US 2011/0297313 A1Published application
Method for preparing transparent multilayer film structures having a perfluorinated copolymer resin layer
AssigneeE. I. Du Pont de Nemours and Company
InventorSAM LOUIS SAMUELS
Life of this patent
Estimating the term…
Abstract
Disclosed is a method for preparing a multilayer film laminate having a first film layer comprising a perfluorinated copolymer resin layer adhered to a polymeric second film layer that has been surface treated with an aminosilane. The multilayer laminate is useful as a photovoltaic module component. Methods for preparing photovoltaic modules that include the multilayer laminate are also disclosed.
Claims20
A method for preparing a transparent multilayer film laminate comprising at least a first film layer and a second film layer, the method comprising:
- A. providing a first film layer comprising a perfluorinated copolymer resin composition wherein i) the perfluorinated copolymer resin consists essentially of copolymerized units of tetrafluoroethylene and at least one perfluorinated comonomer and ii) at least one surface of the first film layer has been modified by a surface treatment;
- B. providing a second film layer comprising a polymeric material selected from the group consisting of α-olefin ethylenically unsaturated carboxylic acid copolymers, ionomers of α-olefin ethylenically unsaturated carboxylic acid copolymers, ethylene vinyl acetate copolymers, poly(vinyl acetals), polyurethanes, polyvinylchlorides, polyethylenes, polyolefin block copolymer elastomers, copolymers of α-olefins and ethylenically unsaturated carboxylic acid esters, silicone elastomers, epoxy resins, and combinations of two or more thereof;
- C. treating a surface of the second film layer with an aminosilane coupling agent to provide a surface-treated second film layer;
- D. contacting a treated surface of the surface-treated second film layer with the modified surface of the first film layer;
- and
- E. adhering the first film layer to the second surface-treated film layer by the application of heat and optionally pressure or vacuum to form a multilayer film laminate;
- wherein the multilayer film laminate is characterized by (i) having an average peel strength between the first film layer and the second surface-treated film layer of greater than 2 lbf/in, measured after exposing the multilayer film laminate to conditions of 85° C. and 85% relative humidity for 1000 hours with the proviso that when the second film layer comprises an ethylene vinyl acetate copolymer, the multilayer film laminate is maintained at a sufficient temperature for a time sufficient to crosslink the ethylene vinyl acetate copolymer prior to exposing the multilayer film laminate to conditions of 85° C. and 85% relative humidity for 1000 hours;
- and (ii) having a light transmission level, as a percentage of the light transmitted through air at wavelengths from 400 to 800 nm, as determined according to methods in ASTM E424, that exceeds that of a comparison standard laminate wherein the multilayer film laminate and the comparison standard laminate have the same structure and composition with the exception that the first film layer of the comparison standard laminate comprises an ethylene tetrafluoroethylene copolymer resin, the compositions of the first film layers of the multilayer film laminate and the comparison standard laminate being otherwise identical.
5 more elements
A method for preparing a photovoltaic module, the method comprising the steps:
- A. providing a solar cell layer;
- B. providing a transparent multilayer film laminate that is larger in area than the solar cell layer, the multilayer film laminate comprising at least a first film layer and a second film layer, wherein
- 1. the first film layer comprises a perfluorinated copolymer resin composition wherein i) the perfluorinated copolymer resin consists essentially of copolymerized units of tetrafluoroethylene and at least one perfluorinated comonomer and ii) at least one surface of the first film layer has been modified by a surface treatment;
- 2. the second film layer comprises a polymeric material selected from the group consisting of α-olefin ethylenically unsaturated carboxylic acid copolymers, ionomers of α-olefin ethylenically unsaturated carboxylic acid copolymers, ethylene vinyl acetate copolymers, poly(vinyl acetals), polyurethanes, polyvinylchlorides, polyethylenes, polyolefin block copolymer elastomers, copolymers of α-olefins and ethylenically unsaturated carboxylic acid esters, silicone elastomers, epoxy resins, and combinations of two or more thereof, wherein a surface of the second film layer has been treated with an aminosilane coupling agent to provide a surface-treated second film layer;
- and
- 3. the multilayer film laminate is characterized by (i) having an average peel strength between the first film layer and the second surface-treated film layer of greater than 2 lbf/in, measured after exposing the multilayer film laminate to conditions of 85° C. and 85% relative humidity for 1000 hours, with the proviso that when the second film layer comprises an ethylene vinyl acetate copolymer, the ethylene vinyl acetate is a crosslinked ethylene vinyl acetate;
- and (ii) having a light transmission level, as a percentage of the light transmitted through air at wavelengths from 400 to 800 nm, as determined according to methods in ASTM E424, that exceeds that of a comparison standard laminate wherein the multilayer film laminate and the comparison standard laminate have the same structure and composition with the exception that the first film layer of the comparison standard laminate comprises an ethylene tetrafluoroethylene copolymer resin, the compositions of the first film layers of the multilayer film laminate and the comparison standard laminate being otherwise identical;
- C. overlaying the solar cell layer with the multilayer film laminate such that
- 1. a surface of the second film layer of the multilayer film laminate contacts the solar cell layer;
- 2. a portion of the second film layer of the multilayer film laminate extends beyond the perimeter of the solar cell layer;
- and
- 3. the portion of the second film layer of the multilayer film laminate that extends beyond the perimeter of the solar cell layer contacts an additional layer that is an encapsulant layer;
- and
- D. adhering the second film layer of the multilayer film laminate to the solar cell layer and the encapsulant layer by the application of heat and optionally pressure or vacuum to provide a photovoltaic module.
11 more elements
A method for preparing a photovoltaic module comprising a multilayer laminate, the method comprising the steps:
- A. providing a solar cell layer;
- B. providing a first film layer comprising a perfluorinated copolymer resin composition wherein i) the perfluorinated copolymer resin consists essentially of copolymerized units of tetrafluoroethylene and at least one perfluorinated comonomer and ii) at least one surface of the first film layer has been modified by a surface treatment;
- C. providing a second film layer having an upper and a lower surface, the second film layer being larger in area than the solar cell layer, wherein the second film layer comprises a polymeric material selected from the group consisting of α-olefin ethylenically unsaturated carboxylic acid copolymers, ionomers of α-olefin ethylenically unsaturated carboxylic acid copolymers, ethylene vinyl acetate copolymers, poly(vinyl acetals), polyurethanes, polyvinylchlorides, polyethylenes, polyolefin block copolymer elastomers, copolymers of α-olefins and ethylenically unsaturated carboxylic acid esters, silicone elastomers, epoxy resins, and combinations of two or more thereof;
- D. treating the upper surface of the second film layer with an aminosilane coupling agent to provide a surface-treated second film layer;
- E. contacting a modified surface of the first film layer with a treated upper surface of the surface-treated second film layer;
- F contacting the solar cell layer with the second film layer such that
- 1. the lower surface of the second film layer contacts the solar cell layer;
- 2. a portion of the second film layer extends beyond the perimeter of the solar cell layer;
- and
- 3. the portion of the second film layer that extends beyond the perimeter of the solar cell layer contacts another layer that is an encapsulant layer;
- and
- G. adhering the second film layer to the first film layer, the solar cell layer and the encapsulant layer by the application of heat and optionally pressure or vacuum to provide a photovoltaic module;
- wherein the photovoltaic module is characterized by (i) having an average peel strength between the first film layer and the second surface-treated film layer of greater than 2 lbf/in, measured after exposing the photovoltaic module to conditions of 85° C. and 85% relative humidity for 1000 hours with the proviso that when the second film layer comprises an ethylene vinyl acetate copolymer, the photovoltaic module is maintained at a sufficient temperature for a time sufficient to crosslink the ethylene vinyl acetate copolymer prior to exposing the photovoltaic module to conditions of 85° C. and 85% relative humidity for 1000 hours;
- and (ii) having a light transmission level, as a percentage of the light transmitted through air at wavelengths from 400 to 800 nm, as determined according to methods in ASTM E424, that exceeds that of a comparison standard laminate wherein the multilayer film laminate and the comparison standard laminate have the same structure and composition with the exception that the first film layer of the comparison standard laminate comprises an ethylene tetrafluoroethylene copolymer resin, the compositions of the first film layers of the multilayer film laminate and the comparison standard laminate being otherwise identical.
11 more elements