The present invention relates to a process for producing a structured porous material comprising a structured inorganic framework made up of metal-oxide based walls in which nanoparticles of metal 0 are incorporated, which comprises the following steps: a) formation of a suspension of hydrophilic nanoparticles of metal 0 stabilized by non-exchangeable ligands that give the nanoparticles their hydrophilic character; b) growth of the inorganic framework from an inorganic precursor around the nanoparticles of metal 0 stabilized by the non-exchangeable hydrophilic ligands, in the presence of a pore-forming agent; and c) elimination of the pore-forming agent and at least partially of the non-exchangeable ligands that give the nanoparticles their hydrophilic character.
1- A process for producing a structured porous material comprising a structured inorganic framework made up of metal-oxide-based walls in which particles of metal 0 are incorporated, said material being characterized by the presence of at least one diffraction peak in a small-angle X-ray powder diffractogram associated with a spatial repeat period of the structured system that corresponds to the periodicity of the pores within the material, which process, comprises the following steps:
2- The process as claimed in claim 1, characterized in that the non-exchangeable ligands are silanes, stannic derivatives or stannous derivatives in which the silicon or tin atom acts as the point where the ligand is anchored onto the metal particle.
3- The process as claimed in claim 1, characterized in that the non-exchangeable ligands comprise a germanium atom that acts as the point where the ligand is anchored onto the metal particle.
4- The process as claimed in claim 1, characterized in that the thickness of the walls is greater than 3 nm and preferably lies in the range from 5 to 15 nm.
5- The process as claimed in claim 1, characterized in that the structuration of the porous material is of the vermicular, lamellar, hexagonal (1D or 2D) or cubic type.
6- The process as claimed in claim 1, characterized in that the non-exchangeable ligands comprise polar or polarizable groups, especially chosen from halogen atoms, such as chlorine, or amine, ammonium, phosphonate, phosphonium, hydroxide, thiol, sulfonate, nitrate, carbonate and alcohol groups, which give the particles their hydrophilic character.
7- The process as claimed in claim 1, characterized in that the non-exchangeable ligands are chosen from 3-chloropropylsilane, N-(3-silylpropyl)imidazole, chlorobenzylsilane, chlorodimethylsilane, N-(3-silylpropyl)alkylimidazolium salts or N-(3-silylpropyl)arylimidazolium salts, N-(benzylsilyl)imidazole, N-(benzylsilyl)alkylimidazolium salts or N-(benzylsilyl)arylimidazolium salts, and also N-(benzylsilyl)trialkylammonium salts or dibutyl-4,7,10-trioxaundecylstannane.
8- The process as claimed in claim 1, characterized in that the inorganic framework consists of silica, a silica/titanium oxide mixture or a silica/alumina mixture.
9- The process as claimed in claim 1, characterized in that the metal particles are platinum, ruthenium, gold, nickel, cobalt, iron, silver, palladium or rhodium particles.
10- The process as claimed in claim 1, characterized in that the metal framework is grown by a sol-gel process.
11- The process as claimed in claim 1, characterized in that the inorganic precursor is a metal or metalloid alkoxide or hydroxide, preferably a titanium or aluminum silicate, tetraalkoxysilane, or tetraalkoxide.
12- The process as claimed in claim 1, characterized in that the framework is grown in an aqueous medium or an aqueous medium mixed with at least one cosolvent chosen from alcohols, preferably linear alcohols such as butanol, ethers such as THF, and dimethylformamide.
13- The process as claimed in claim 1, characterized in that the framework is grown at a temperature ranging from 0° C. to 100° C., preferably from 20° C. to 65° C.
14- The process as claimed in claim 1, characterized in that the framework is grown with a molar (metal of the inorganic precursor/pore-forming agent) ratio of 30-300.
15- The process as claimed in claim 1, characterized in that the framework is grown with a (metal of the particles/metal of the inorganic precursor) weight ratio of less than 10%, preferably from 0.001% to 5% and preferentially from 0.005 to 5%.
16- The process as claimed in claim 1, characterized in that the framework is grown in a medium having a pH of 0 to 10 and preferably 0 to 4.
17- The process as claimed in claim 1, characterized in that the framework is grown in the presence of a hydrolysis-polycondensation catalyst of the acid, base or nucleophilic type and preferably such as HO (acid type), NH3, KOH, or NaOH (base type) or NaF or TBAF (nucleophilic type).
18- The process as claimed in claim 1, characterized in that the pore-forming agent is chosen from:
19- The process as claimed in claim 1, characterized in that the pore-forming agent is eliminated by heat treatment or by degradation in an aqueous medium under UV irradiation, or in the presence of a metal salt.
20- The process as claimed in claim 1, characterized in that, prior to growth of the framework, a colloidal suspension of particles of metal 0 rendered hydrophilic and stabilized by non-exchangeable ligands is produced, to which a core-forming agent, preferably in a water/THF mixture, is added.
21- A structured porous material that can be obtained as claimed in claim 1, comprising a structured framework made up of metal-oxide-based walls in which particles of metal 0 are incorporated.
22- The material as claimed in claim 21, characterized in that it has a specific surface area of 20 to 1200 m2/g and preferably 300 to 1100 m2/g in the case of a framework made up predominantly of silica.
23- The material as claimed in claim 21 characterized in that the size of the walls is greater than 3 nm and, preferably in the range from 5 to 15 nm.
24- The material as claimed in claim 21, characterized in that inorganic framework is made up of at least one metal or an oxide of a metal of groups 3 to 11, or of at least one oxide of a metalloid of groups 2 and 12 to 14, or of a mixture of various metals or metal oxides or of a mixture of these oxides, especially those chosen form silicon, aluminum, titanium, tin, tantalum or zirconium.
25- The material as claimed in claim 21 characterized in that the inorganic framework is made up of silica or a mixed, silica/titanium oxide or silica/alumina, oxide (especially aluminosilicates).
26- The material as claimed in claim 21 characterized in that it has a microporosity, a mesoporosity or a mixed microporosity/mesoporosity.