High strength steel sheet with good wettability and manufacturing method thereof

Abstract

The present disclosure relates to a high strength steel sheet having good wettability, a tensile strength of 590 MPa or more and a strength-ductility balance (TS×El) of 16,520 MPa·% or more, and a manufacturing method thereof. The high strength steel comprises, in % by weight, C: 0.03˜0.1%, Si: 0.005˜0.105%, Mn: 1.0˜3.0%, P: 0.005˜0.04%, S: 0.003% or less, N: 0.003˜0.008%, Al: 0.05˜0.4%, Mo or Cr satisfying the inequality 10≦50·[Mo %]+100·[Cr %]≦30, at least one of Ti: 0.005˜0.020%, V: 0.005˜0.050% and B: 0.0005˜0.0015%, and the balance of Fe and unavoidable impurities, wherein a microstructure of the steel sheet is a multi-phase structure comprising, in an area ratio of cross-sectional structure, 70% or more ferrite phase having a Vickers hardness Hv of 120˜250 and 10% or more martensite phase having a Vickers hardness Hv of 321˜555.