Crystallized material with hierarchical porosity containing silicon

Abstract

Hierarchical porosity material consisting of at least two elementary spherical particles having a maximum diameter of 200 microns, at least one of said spherical particles comprises at least one matrix based on silicon oxide and exhibiting crystallized walls, said material having a macropore volume measured by mercury porosimetry ranging between 0.05 and 1 ml/g, a mesopore volume measured by nitrogen volumetric analysis ranging between 0.01 and 1 ml/g and a micropore volume measured by nitrogen volumetric analysis ranging between 0.03 and 0.4 ml/g. The preparation of said material and use of same as adsorbent or as acidic solid is also described.