Method of preparing a green-ceramic pigment for reduction firing using copper oxide and a green ceramic made thereby
AssigneeMyongji University Industry and Academia Cooperation Foundation
InventorByung-Ha Lee
Life of this patent
Estimating the term…
Abstract
A method of preparing a green-ceramic pigment for reduction firing using copper oxide that includes mixing tin oxide (SnO2) and copper oxide (CuO); providing a fired product by applying oxidation firing to the mixture at a firing temperature of 1000 to 1300° C.; and grinding the fired product. Aspects also provide a green-ceramic pigment prepared by this method, as well as a method of manufacturing a green ceramic.
Claims7
A method of preparing a green-ceramic pigment using copper oxide for reduction firing, the method comprising:
- mixing tin oxide (SnO2) and copper oxide (CuO);
- providing a fired product by applying oxidation firing to the mixture at a firing temperature of 1000 to 1300° C.;
- and
- grinding the fired product.
1 more element
A method of manufacturing a green ceramic, the method comprising:
- mixing tin oxide (SnO2) and copper oxide (CuO);
- providing a fired product by applying oxidation firing to the mixture at a firing temperature of 1000 to 1300° C.;
- grinding the fired product;
- mixing the ground fired product with glaze;
- and
- applying the glaze mixture to a ceramic and subjecting the ceramic to reduction firing.