Crosslinkable theromoplastic olefin elastomers and crosslinked thermoset olefin elastomer obtained therefrom

Abstract

Thermoset polyolefin elastomer obtained by static curing with water a silane-grafted thermoplastic heterophasic polyolefin composition (I) having a flexural modulus equal to or lower than 150 MPa, and comprising: (a) a crystalline propylene homopolymer or copolymer of propylene with up to 15% by weight of ethylene or other alpha-olefin comonomer(s), or their combinations, and (b) a copolymer or a composition of copolymers of ethylene with other alpha-olefins containing from 15% by weight to less then 40% by weight of ethylene; said thermoset polyolefin elastomer having a compression set value of from 30 to 65%, a ratio of elongation at break to compression set values of above 8, and hardness shore A values below 90.