High-strength spring steel excellent in brittle fracture resistance and method for producing same

Abstract

A spring steel having a high strength of 1900 MPa or more and superior in the brittle fracture resistance, as well as a method for manufacturing the same, are provided. The high strength spring steel comprises, as basic components in mass %, C: 0.4-0.6%, Si: 1.4-3.0%, Mn: 0.1-1.0%, Cr: 0.2-2.5%, P: 0.025% or less, S: 0.025% or less, N: 0.006% or less, Al: 0.1% or less, and O: 0.003% or less, the amount of solute C being 0.15% or less, the amount of Cr contained as a Cr-containing precipitate being 0.10% or less, and a TS value represented by the following equation being 24.8% or more, and in point of structure, the pre-austenite grain diameter being 10 μm or smaller, wherein TS=28.5*[C]+4.9*[Si]+0.5*[Mn]+2.5*[Cr]+1.7*[V]+3.7*[Mo] where [X] stands for mass % of element X.

Dependencies are inferred from the claim text.