# US 2010/0168338 A1 · Method for preparing a polymeric material including a multiblock copolymer prepared by controlled free-radical polymerisation

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 2010/0168338 A1
- Document ID: US20100168338A1
- Status: Published application
- Kind: A1
- Application number: 12/063,063
- Filed: 2006-08-08
- Published: 2010-07-01
- Earliest claimed: 2005-08-09
- Inventors: Olivier Guerret
- Web page: https://patentgrep.com/patent/US20100168338A1

## CPC

- C08F 293/005: {using free radical "living" or "controlled" polymerisation, e.g. using a complexing agent}
- C08F 2/001: {Multistage polymerisation processes characterised by a change in reactor conditions without deactivating the intermediate polymer (C08F295/00, C08F297/00 take precedence)}
- C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS

## Abstract

A method for preparing a polymeric material including a multiblock copolymer with n blocks, where n is an integer no lower than 2, which method comprises at least one cycle of steps including (a) a step of synthesising a block by performing controlled free-radical polymerisation of one or more free-radical polymerisable monomers, and (b) a step of polymerising the monomers that were not converted during step (a) into a polymer having a number-average molecular weight lower than the number-average molecular weight of said block, wherein said cycle of steps is carried out at least for the (n−1) first blocks.

## Claims

### Claim 1

A method for preparing a polymeric material comprising a multiblock copolymer comprising n blocks, where n is an integer greater than or equal to 2, said method comprising at least one cycle of steps comprising:
a) a step of synthesizing a block by controlled free-radical polymerization of one or more free-radical-polymerizable monomers; and
b) a step of polymerizing monomers that were not converted during step a) into a polymer having a number-average molecular weight lower than the number-average molecular weight of said block;
wherein said cycle of steps is carried out at least for the first n−1 blocks.

### Claim 2 (depends on 1)

The method as claimed in claim 1, in which the cycle of steps is carried out for the n blocks.

### Claim 3

A method for preparing a polymeric material comprising a copolymer comprising at least one block A and at least one block B, said method comprising successively:
a) a step of polymerizing one or more free-radical-polymerizable monomers by controlled free-radical polymerization, so as to form block A;
b) a step of polymerizing the monomers that were not converted during step a), so as to form a polymer of chemical nature identical to block A but having a number-average molecular weight lower than that of block A;
c) a step of adding to the medium resulting from steps a) and b) one or more free-radical-polymerizable monomers that are precursors of block B;
d) a step of polymerizing said monomers that are precursors of block B by controlled free-radical polymerization, said block B being linked to block A by covalent bonding; and
e) optionally, a step of polymerizing the monomers that were not converted during step d), so as to form a polymer of chemical nature identical to block B but having a number-average molecular weight lower than that of block B.

### Claim 4 (depends on 1)

The method as claimed in claim 1, carried out in emulsion, in bulk or in an organic solvent.

### Claim 5 (depends on 1)

The method as claimed in claim 1, in which step a) is carried out by stable free-radical polymerization.

### Claim 6 (depends on 5)

The method as claimed in claim 5, in which the stable free-radical polymerization is carried out in the presence of at least one alkoxyamine chosen from the monoalkoxyamines of formula (I):
in which:
R1 and R3, which may be identical or different, represent a linear or branched alkyl group containing a number of carbon atoms ranging from 1 to 3;
R2 represents a hydrogen atom, an alkali metal, an ammoniumion, a linear or branched alkyl group containing a number of carbon atoms ranging from 1 to 8, or a phenyl group.

### Claim 7 (depends on 6)

The method as claimed in claim 6, in which the alkoxyamine corresponds to the formula below:

### Claim 8 (depends on 5)

The method as claimed in claim 5, in which the stable free-radical polymerization is carried out in the presence of at least one polyalkoxyamine derived from a method consisting in reacting one or more alkoxyamines of formula (I) below:
in which:
R1 and R3, which may be identical or different, representing a linear or branched alkyl group containing a number of carbon atoms ranging from 1 to 3;
R2 representing a hydrogen atom, a linear or branched alkyl group containing a number of carbon atoms ranging from 1 to 8, a phenyl group, an alkali metal, or an ammonium ion;
with at least one polyunsaturated compound of formula (II):
in which Z represents an aryl group or a group of formula Z1—[X—C(O)]n, in which Z1 represents a polyfunctional structure, X is an oxygen atom, a nitrogen atom bearing a carbon-based group or an oxygen atom, or a sulfur atom, and n is an integer greater than or equal to 2, in the presence or absence of solvent(s),
at a temperature ranging, from 0 to 90° C.,
the molar ratio between monoalkoxyamines of formula (I) and polyunsaturated compounds of formula II ranging from 1.5 to 1.5 n;
this step being optionally followed by a step of evaporating the possible solvents.

### Claim 9 (depends on 8)

The method as claimed in claim 8, in which the polyalkoxyamine corresponds to the formula below:

### Claim 10 (depends on 6)

The method as claimed in claim 6, in which the alkoxyamine is introduced into the polymerization medium in a proportion of 0.01% to 10% by mass relative to the mass of monomers.

### Claim 11 (depends on 1)

The method as claimed in claim 1, in which the free-radical-polymerizable monomers are chosen from monomers having a carbon-carbon double bond capable of free-radical polymerization.

### Claim 12 (depends on 11)

The method as claimed in claim 11, in which the monomers having a carbon-carbon double bond capable of free-radical polymerization are chosen from vinylaromatic monomers, dienes, acrylic monomers, alkyl acrylates, cycloalkyl acrylates or aryl acrylates, hydroxyalkyl acrylates, alkyl ether acrylates, alkoxy- or aryloxy-polyalkylene glycol acrylates, ethoxypolyethylene glycol acrylates, methoxypolypropylene glycol acrylates, methoxypolyethylene glycol-polypropylene glycol acrylates, or mixtures thereof, aminoalkyl acrylates, acrylates of amine salts, fluorinated acrylates, silylated acrylates, phosphorus-containing acrylates, methacrylic monomers, alkyl methacrylates, cycloalkyl methacrylates, alkenyl methacrylates, aryl methacrylates, hydroxyalkyl methacrylates, alkyl ether methacrylates, alkoxy- or aryloxy-polyalkylene glycol methacrylates, aminoalkyl methacrylates, methacrylates of amine salts, fluorinated methacrylates, silylated methacrylates, phosphorus-containing methacrylates, hydroxyethylimidazolidone methacrylate, hydroxyethylimidazolidinone methacrylate, 2-(2-oxo-1-imidazolidinyl)ethyl methacrylate, acrylonitrile, acrylamide or substituted acrylamides, 4-acryloylmorpholine, N-methylolacrylamide, acrylamidopropyltrimethylammonium chloride (APTAC), acrylamidomethylpropanesulfonic acid (AMPS) or its salts, methacrylamide or substituted methacrylamides, N-methylol methacrylamide, methacrylamidopropyltrimethylammonium chloride (MAPTAC), itaconic acid, maleic acid or its salts, maleic anhydride, alkyl maleates or hemimaleates, alkoxy- or aryloxy-polyalkylene glycol maleates or hemimaleates, vinylpyridine, vinylpyrrolidinone, (alkoxy) poly(alkylene glycol) vinyl ether or (alkoxy) poly(alkylene glycol) divinyl ether, poly(ethylene glycol) divinyl ether, olefinic monomers, fluorinated olefinic monomers, and vinylidene monomers, alone or as a mixture of at least two abovementioned monomers.

### Claim 13 (depends on 1)

The method as claimed in claim 1, in which step a) is, when the method is carried out in emulsion, carried out in the presence of at least one anionic, cationic or nonionic emulsifier.

### Claim 14 (depends on 13)

The method as claimed in claim 13, in which the emulsifier is chosen from alkyl sulfates, aryl sulfates, alkyl sulfonates, aryl sulfonates, fatty acid salts, polyvinyl alcohols or polyethoxylated fatty alcohols.

### Claim 15 (depends on 1)

The method as claimed in claim 1, in which each step b) is carried out in the presence of a free-radical polymerization initiator chosen from peroxide compounds, persulfate compounds, azo compounds or redox compounds.

### Claim 16 (depends on 1)

The method as claimed in claim 1, in which step b) is carried out at a polymerization temperature at least 20° C. below that of each step a).

### Claim 17 (depends on 1)

The method as claimed in claim 1, in which each step b) is carried out in the presence of at least one transfer agent chosen from sulfur compounds, alcohol compounds, or transfer agents used for free-radical polymerization of the reversible addition fragmentation transfer type.

### Claim 18 (depends on 17)

The method as claimed in claim 17, in which the sulfur compounds are chosen from mercaptan compounds containing at least 4 carbon atoms and disulfide compounds.

### Claim 19 (depends on 17)

The method as claimed in claim 17, in which the alcohol compounds are chosen from hindered phenols and secondary alcohols.

### Claim 20 (depends on 17)

The method as claimed in claim 17, in which the transfer agents used for the free-radical polymerization of the reversible addition fragmentation transfer type are chosen from trithiocarbonates, xanthates, dithioesters and dithiocarbamates.

### Claim 21 (depends on 1)

The method as claimed in claim 1, in which the polymeric material is a material comprising a diblock copolymer.

### Claim 22 (depends on 21)

The method as claimed in claim 21, in which the diblock copolymer is a (poly(n-butyl acrylate)-b-poly(methyl methacrylate)) copolymer.

### Claim 23 (depends on 1)

A polymeric material obtained by a method as defined in claim 1, comprising a multiblock copolymer comprising n blocks connected to one another by covalent bonding, n being an integer greater than or equal to 2, and for at least each of the first (n−1) blocks, polymer chains formed from the residual monomers that go to make up the corresponding block, said chains having a number-average molecular weight lower than that of the corresponding block.

### Claim 24 (depends on 23)

The polymeric material as claimed in claim 23, comprising polymer chains formed from the residual monomers that go to make up the corresponding block, said chains having a number-average molecular weight lower than that of the corresponding block for each of the n blocks.

### Claim 25 (depends on 23)

The use of a material as defined in claim 23, as a thermoplastic.

### Claim at position 26

26-29. (canceled)

### Claim 30 (depends on 3)

The method as claimed in claim 3, carried out in emulsion, in bulk or in an organic solvent.

### Claim 31 (depends on 3)

The method as claimed in claim 3, in which each step a) and b) is carried out by stable free-radical polymerization.

### Claim 32 (depends on 3)

The method as claimed in claim 3, in which each step a) and b) are, when the method is carried out in emulsion, carried out in the presence of at least one anionic, cationic or nonionic emulsifier.

### Claim 33 (depends on 3)

The method as claimed in claim 3, in which each step b) and e) are carried out in the presence of a free-radical polymerization initiator chosen from peroxide compounds, persulfate compounds, azo compounds or redox compounds.

### Claim 34 (depends on 3)

The method as claimed in claim 3, in which each step b) and e) are carried out at a polymerization temperature at least 20° C. below that of each of steps a) and d).

### Claim 35 (depends on 3)

The method as claimed in claim 3, in which each step b) and e) are carried out in the presence of at least one transfer agent chosen from sulfur compounds, alcohol compounds, or the transfer agents used for free-radical polymerization of the reversible addition fragmentation transfer type.

### Claim 36 (depends on 35)

The method as claimed in claim 35, in which the sulfur compounds are chosen from mercaptan compounds containing at least 4 carbon atoms and disulfide compounds.

### Claim 37 (depends on 35)

The method as claimed in claim 35, in which the alcohol compounds are chosen from hindered phenols and secondary alcohols.

### Claim 38 (depends on 35)

The method as claimed in claim 35, in which the transfer agents used for the free-radical polymerization of the reversible addition fragmentation transfer type are chosen from trithiocarbonates, xanthates, dithioesters and dithiocarbamates.

### Claim 39 (depends on 3)

The method as claimed in claim 3, in which the polymeric material is a material comprising a diblock copolymer.

### Claim 40 (depends on 39)

The method as claimed in claim 39, in which the diblock copolymer is a (poly(n-butyl acrylate)-b-poly(methyl methacrylate)) copolymer.

### Claim 41 (depends on 3)

A polymeric material obtained by a method as defined in claim 3, comprising a multiblock copolymer comprising n blocks connected to one another by covalent bonding, n being an integer greater than or equal to 2, and for at least each of the first (n−1) blocks, polymer chains formed from the residual monomers that go to make up the corresponding block, said chains having a number-average molecular weight lower than that of the corresponding block.

### Claim 42 (depends on 41)

The polymeric material as claimed in claim 41, comprising polymer chains formed from the residual monomers that go to make up the corresponding block, said chains having a number-average molecular weight lower than that of the corresponding block for each of the n blocks.