Non-woven sheet containing fibers with sheath/core construction
AssigneeE. I. Du Pont de Nemours and Company
InventorsDavid Matthews Laura, JR., Xun Ma, Paul Ellis Rollin, JR.
Life of this patent
Estimating the term…
Abstract
A non-woven sheet contains sheath/core polymer fibers with the polymer in the sheath having a melting point at least 15 degrees centigrade higher than the melting point of the polymer of the core. Preferably, the polymer of the sheath is polyphenylenesulfide and the polymer of the core is polyethyleneterephthlate. The nonwoven sheet can be used with a film to make a composite laminate suitable for use in electrical insulation.
Claims15
A non-woven sheet comprising:
- a network of substantially-continuous thermoplastic polymer filaments, the polymer filaments each individually comprising a plurality of polymers including at least a first polymer and a second polymer, the melting point of the first polymer being at least 15 degrees C. higher than the melting point of the second polymer, the individual polymer filaments further characterized in that
- (1) the first polymer comprises from 10 to 70 weight percent of the total weight of the first and second polymer,
- (2) the second polymer comprises from 30 to 90 weight percent of the total weight of the first and second polymer and,
- the network of filaments being consolidated and fused such that
- (a) the first polymer forms a continuous phase in the fused consolidated network and
- (b) the second polymer forms a disperse phase in the fused consolidated network.
Insulation useful for an electrical device comprising one or more non-woven sheets positioned adjacent to, and attached to at least one side of a polymeric film, said non-woven sheets comprising:
- a network of substantially-continuous thermoplastic polymer filaments, the polymer filaments each individually comprising a plurality of polymers including at least a first polymer and a second polymer, the melting point of the first polymer being at least 15 degrees C. higher than the melting point of the second polymer, the individual polymer filaments further characterized in that
- (1) the first polymer comprises from 10 to 70 weight percent of the total weight of the first and second polymer,
- (2) the second polymer comprises from 30 to 90 weight percent of the total weight of the first and second polymer and,
- the network of filaments being consolidated and fused such that
- (a) the first polymer forms a continuous phase in the fused consolidated network and
- (b) the second polymer forms a disperse phase in the fused consolidated network.
A method for producing a non-woven sheet of multicomponent polymeric fiber comprising the steps of:
- (i) melt spinning at between 3500 to 5000 m/min in the presence of an attenuating force provided by a rectangular slot jet a fiber having an average fiber diameter greater than 7 microns, said fiber further comprising an amorphous sheath component of from 10 to 70 weight percent of a first polymer based on the total weight of polymer in the core and sheath and a core component of from 30 to 90 weight percent of a fibrous second polymer based on the total weight of polymer in the core and sheath, wherein the melting point of the first polymer is at least 15 degrees C. higher than the melting point of the second polymer,
- (ii) forming a non-woven web of fibers on a forming belt,
- (iii) passing the non-woven web of fibers through heated bonding rolls to fuse the fibers and thereafter,
- (iv) smooth calendering said fused fiber web to convert the amorphous sheath of first polymer material into a substantially crystalline continuous phase and further compact and densify the non-woven web to embed the fibrous second polymer into the continuous phase of the first polymer.
Dependencies are inferred from the claim text.