Curable resin composition for hard coat layer and hard coat film

Abstract

The invention provides a hard coat film with transparency and mar-proofness, obtained by coating, drying and curing on a transparent base film a curable resin composition for a hard coat layer comprising (1) reactive inorganic fine particles A, (2) hydrophilic fine particles B and (3) a curable reactive matrix containing a binder component C that has a reactive functional group c with crosslinking reactivity for the reactive inorganic fine particles A, wherein the content of the hydrophilic fine particles B is 0.1-5.0 wt % with respect to the total solid content, and desired irregularities are formed in the hard coat layer surface, preferably with raised sections having heights of from 3 nm to 50 nm, and spacings between the raised sections of 50 nm-5 μm.