Back to results
US 2010/0140441 A1Published application
Method for reducing vibrations from a motor vehicle exhaust system
AssigneeE.I. du Pont de Nemours and Company
InventorsChristophe Chervin, Orvar E. Otterstedt, Mark S. Jacobson
Life of this patent
Estimating the term…
Abstract
Methods for reducing vibration or noise from the exhaust system of a motor vehicle, especially of an automobile, by producing a thermoplastic vulcanizate muffler hanger and mounting it between the exhaust system and the body of the motor vehicle. Also, the thermoplastic vulcanizate muffler hangers so produced.
Claims16
A method for reducing vibration from an exhaust system of a motor vehicle, comprising:
- extruding a thermoplastic vulcanizate polymer through a die having the shape of a muffler hanger;
- slicing the extruded thermoplastic vulcanizate polymer to yield a muffler hanger of desired thickness;
- and
- mounting the muffler hanger between the exhaust system and the body of the motor vehicle,
- wherein the thermoplastic vulcanizate polymer is selected from the group consisting of:
- I) a TPV comprising:
- (A) from at or about 15 to or about 60 wt-% of a polyalkylene phthalate polyester polymer or copolymer continuous phase, and
- (B) from at or about 40 to or about 85 wt-% of a polyethylene/(meth)acrylate rubber dispersed phase,
- wherein:
- the weight percentages are based on the total weight of the thermoplastic vulcanizate polymer, and
- the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent;
- (II) a TPV comprising:
- (A) from at or about 25 to or about 60% wt-% of a polyamide resin, and
- (B) from at or about 75 to 40% wt-% of a rubber component;
- wherein:
- the weight percentages are based on the total weight of the thermoplastic vulcanizate polymer,
- the rubber component comprises
- from at or about 20 to or about 80 wt-% of a hydrogenated nitrile group containing rubber and
- from at or about 80 to or about 20 wt-% of an acrylic rubber and
- is dispersed in the form of cross-linked particles in said polyamide resin,
- the hydrogenated nitrile group containing rubber is
- a hydrogenated copolymer comprising
- from at or about 10 to or about 60 wt-% of a vinyl nitrile,
- from at or about 15 to or about 90 wt-% of a conjugated diene and
- from at or about 0 to or about 75 wt-% of a monomer copolymerizable with vinyl nitrile and the conjugated diene, and
- has an iodine value of 120 or less,
- the acrylic rubber is
- a copolymer of at least one acrylate selected from the group consisting of
- an alkyl acetate and an alkoxy-substituted alkyl acrylate
- with at least one compound selected from the group consisting of
- a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group containing (meth)acrylate, an epoxy group containing ethylenically unsaturated compound, an active halogen containing ethylenically unsaturated compound and a carboxyl group containing ethylenically unsaturated compound;
- (III) a TPV made by a method comprising:
- (I) mixing:
- (A) a rheologically-stable polyamide resin having
- a melting point or glass transition temperature at or about 25° C. to about 275° C.,
- (B) a silicone base comprising:
- (B′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule, and
- (B″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of the silicone base to the polyamide resin being greater than 35:65 to 85:15,
- (C) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from:
- (i) from 0.1 to 5 parts by weight of a coupling agent
- having a molecular weight of less than 800 and
- containing at least two groups
- independently selected from an ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl and alkoxy,
- having 1 to 20 carbon atoms or oxazoline in its molecule,
- (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having
- at least one group selected from
- epoxy, anhydride, silanol, carboxyl, amine and alkoxy,
- having 1 to 20 carbon atoms or oxazoline in its molecule, and
- (iii) from 0.1 to 10 parts by weight of a copolymer comprising
- at least one diorganopolysiloxane block and at least one block selected from
- polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate,
- (D) an organohydrido silicon compound comprising
- an average of at least 2 silicon-bonded hydrogen groups in its molecule, and
- (E) a hydrosilation catalyst,
- wherein components (D) and (E) are present in an amount sufficient to cure the diorganopolysiloxane (B′);
- and
- (II) dynamically curing the diorganopolysiloxane (B′);
- (IV) a TPV made by a method comprising:
- (i) mixing:
- (A) a thermoplastic resin comprising
- more than 50 percent by volume of a polyester resin and having a softening point at or about 23° C. to or about 300° C.,
- (B) a silicone elastomer comprising:
- (E′) 100 parts by weight of a diorganopolysiloxane gum having
- a plasticity of at least 30 and
- an average of at least 2 alkenyl groups in its molecule and, optionally,
- (E″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15,
- (C) a glycidyl ester compatibilizer,
- (D) an organohydrido silicone compound containing an average of at least 2 silicon-bonded hydrogen groups in its molecule, and
- (E) a hydrosilation catalyst,
- wherein components (D) and (E) are present in an amount sufficient to cure said diorganopolysiloxane (B′), and
- (ii) dynamically vulcanizing said diorganopolysiloxane (E′);
- (V) a TPV comprising:
- (A) from at or about 20 to or about 70 wt-% of a mixture (M) of two or more polyalkylene phthalates,
- (B) from at or about 2 to or about 60 wt-% of a cross-linked acrylate rubber,
- (C) from at or about 0.5 to or about 20 wt-% of an ionomer, and
- (D) from at or about 1 to or about 30 wt-% of a terpolymer of ethylene, butylacrylate (BA) and glycidylmethacrylate (GMA),
- wherein the weight percentages are based on the sum of (A), (B), (C) and (D);
- (VI) a TPV comprising:
- (A) from or about 20 to or about 80 wt-% of a mixture (M) of two or more polyalkylene phthalates,
- (B) from or about 2 to or about 60 wt-% of a cross-linked acrylate rubber,
- (C) from or about 0 to or about 20 wt-% of an ionomer, and
- (D) from or about 0 to or about 30 wt-% of a terpolymer of ethylene, butylacrylate (BA) and glycidylmethacrylate (GMA),
- wherein the weight percentages are based on the sum of (A), (B), (C) and (D);
- and
- (VII) mixtures of TPVs (I) to (VI).
82 more elements
An extruded thermoplastic vulcanizate muffler made by the method comprising the steps of:
- extruding a thermoplastic vulcanizate polymer through a die having the shape of a muffler hanger;
- slicing the extruded thermoplastic vulcanizate polymer to yield a muffler hanger of desired thickness;
- and
- mounting the muffler hanger between the exhaust system and the body of the motor vehicle,
- wherein the thermoplastic vulcanizate polymer is selected from the group consisting of:
- I) a TPV comprising:
- (A) from at or about 15 to or about 60 wt-% of a polyalkylene phthalate polyester polymer or copolymer continuous phase, and
- (B) from at or about 40 to or about 85 wt-% of a polyethylene/(meth)acrylate rubber dispersed phase,
- wherein:
- the weight percentages are based on the total weight of the thermoplastic vulcanizate polymer, and
- the rubber is dynamically cross-linked with a peroxide free radical initiator and an organic diene co-agent;
- (II) a TPV comprising:
- (A) from at or about 25 to or about 60% wt-% of a polyamide resin, and
- (B) from at or about 75 to 40% wt-% of a rubber component;
- wherein:
- the weight percentages are based on the total weight of the thermoplastic vulcanizate polymer,
- the rubber component comprises
- from at or about 20 to or about 80 wt-% of a hydrogenated nitrile group containing rubber and
- from at or about 80 to or about 20 wt-% of an acrylic rubber and
- is dispersed in the form of cross-linked particles in said polyamide resin,
- the hydrogenated nitrile group containing rubber is
- a hydrogenated copolymer comprising
- from at or about 10 to or about 60 wt-% of a vinyl nitrile,
- from at or about 15 to or about 90 wt-% of a conjugated diene and
- from at or about 0 to or about 75 wt-% of a monomer copolymerizable with vinyl nitrile and the conjugated diene, and
- has an iodine value of 120 or less,
- the acrylic rubber is
- a copolymer of at least one acrylate selected from the group consisting of
- an alkyl acetate and an alkoxy-substituted alkyl acrylate
- with at least one compound selected from the group consisting of
- a nonconjugated diene, a conjugated diene, a dihydrodicyclopentadienyl group containing (meth)acrylate, an epoxy group containing ethylenically unsaturated compound, an active halogen containing ethylenically unsaturated compound and a carboxyl group containing ethylenically unsaturated compound;
- (III) a TPV made by a method comprising:
- (I) mixing:
- (A) a rheologically-stable polyamide resin having
- a melting point or glass transition temperature at or about 25° C. to about 275° C.,
- (B) a silicone base comprising:
- (B′) 100 parts by weight of a diorganopolysiloxane gum having a plasticity of at least 30 and having an average of at least 2 alkenyl groups in its molecule, and
- (B″) 5 to 200 parts by weight of a reinforcing filler, the weight ratio of the silicone base to the polyamide resin being greater than 35:65 to 85:15,
- (C) for each 100 parts by weight of said polyamide resin, a compatibilizer selected from:
- (i) from 0.1 to 5 parts by weight of a coupling agent
- having a molecular weight of less than 800 and
- containing at least two groups
- independently selected from an ethylenically unsaturated group, epoxy, anhydride, silanol, carboxyl, hydroxyl and alkoxy,
- having 1 to 20 carbon atoms or oxazoline in its molecule,
- (ii) from 0.1 to 10 parts by weight of a functional diorganopolysiloxane having
- at least one group selected from
- epoxy, anhydride, silanol, carboxyl, amine and alkoxy,
- having 1 to 20 carbon atoms or oxazoline in its molecule, and
- (iii) from 0.1 to 10 parts by weight of a copolymer comprising
- at least one diorganopolysiloxane block and at least one block selected from
- polyamide, polyether, polyurethane, polyurea, polycarbonate and polyacrylate,
- (D) an organohydrido silicon compound comprising
- an average of at least 2 silicon-bonded hydrogen groups in its molecule, and
- (E) a hydrosilation catalyst,
- wherein components (D) and (E) are present in an amount sufficient to cure the diorganopolysiloxane (B′);
- and
- (II) dynamically curing the diorganopolysiloxane (B′);
- (IV) a TPV made by a method comprising:
- (i) mixing:
- (A) a thermoplastic resin comprising
- more than 50 percent by volume of a polyester resin and
- having a softening point at or about 23° C. to or about 300° C.,
- (B) a silicone elastomer comprising:
- (E′) 100 parts by weight of a diorganopolysiloxane gum having
- a plasticity of at least 30 and
- an average of at least 2 alkenyl groups in its molecule and, optionally,
- (E″) up to 200 parts by weight of a reinforcing filler, the weight ratio of said silicone elastomer to said thermoplastic resin is from 35:65 to 85:15,
- (C) a glycidyl ester compatibilizer,
- (D) an organohydrido silicone compound containing an average of at least 2 silicon-bonded hydrogen groups in its molecule, and
- (E) a hydrosilation catalyst,
- wherein components (D) and (E) are present in an amount sufficient to cure said diorganopolysiloxane (B′), and
- (ii) dynamically vulcanizing said diorganopolysiloxane (E′);
- (V) a TPV comprising:
- (A) from at or about 20 to or about 70 wt-% of a mixture (M) of two or more polyalkylene phthalates,
- (B) from at or about 2 to or about 60 wt-% of a cross-linked acrylate rubber,
- (C) from at or about 0.5 to or about 20 wt-% of an ionomer, and
- (D) from at or about 1 to or about 30 wt-% of a terpolymer of ethylene, butylacrylate (BA) and glycidylmethacrylate (GMA),
- wherein the weight percentages are based on the sum of (A), (B), (C) and (D);
- (VI) a TPV comprising:
- (A) from or about 20 to or about 80 wt-% of a mixture (M) of two or more polyalkylene phthalates,
- (B) from or about 2 to or about 60 wt-% of a cross-linked acrylate rubber,
- (C) from or about 0 to or about 20 wt-% of an ionomer, and
- (D) from or about 0 to or about 30 wt-% of a terpolymer of ethylene, butylacrylate (BA) and glycidylmethacrylate (GMA),
- wherein the weight percentages are based on the sum of (A), (B), (C) and (D);
- and
- (VII) mixtures of TPVs (I) to (VI).
83 more elements
Dependencies are inferred from the claim text.