Piping member

Abstract

The present invention relates to a piping member molded from a resin composition comprising 50 to 120 parts by mass of a polystyrene-based resin relative to 100 parts by mass of a polyphenylene ether-based resin as essential components, and having a melt flow rate after kneading of 1.0 to 5.0 g/10 min. The present invention also relates to a piping member which has individual characteristics of a mold shrinkage factor from 0.5 to 0.8%, a time to breakage of 1,000 hours or more in a high-temperature creep characteristics test when molding is carried out in an atmosphere at 95° C. under an applied tensile load of 5.0 MPa, and a moisture content of the kneaded resin composition before molding of less than 250 ppm, and in which is further blended a styrene•butadiene-based rubber having a styrene content of 10 to 40% and a weight average molecular weight of 200,000 or more in an amount of 1 to 15 parts by mass relative to 100 parts by mass of the polyphenylene ether-based resin.