Method for forming compact from powder and sintered product
AssigneeDiamet Corporation
InventorsTakashi Nakai, Kinya Kawase
Life of this patent
Estimating the term…
Abstract
A method for forming a compact from a powder wherein a forming portion 1A in a mold body 2 is filled with a raw powder and upper and lower punches 3,4 are fitted into the forming portion 1A to form the compact. Prior to filling the forming portion 1A with the raw powder M, a solution L with a lubricant being uniformly dissolved in a solvent is applied to a peripheral portion of the forming portion 1A, and then the solution is evaporated, thus forming a crystallized layer B thereon. Thus, the reduction of a force for ejecting the compact is realized, while improving the density of the compact, realizing the stable and successive production of the compact.
Claims7
A method for forming a compact from a powder, comprising the steps of:
- applying a solution obtained by dissolving a lubricant in a solvent to a forming portion of a mold body;
- evaporating the solution to form a crystallized layer of the lubricant on a surface of the forming portion;
- filling the forming portion of the mold body with a raw powder, said raw powder being Fe-based metal powder or Cu-based metal powder, and
- then fitting upper and lower punches into the forming portion,
- wherein said lubricant is at least one member selected from the group consisting of dipotassium hydrogen phosphate, disodium hydrogen phosphate, trisodium phosphate, sodium polyphosphate, riboflavin sodium phosphate, potassium sulfate, sodium sulfate, sodium thio sulfate, sodium dodecylsulfate, sodium dodecylbenzenesulfonate, Food Blue No. 1., Food Yellow No. 5., sodium ascorbyl sulfate, sodium tetraborate, sodium silicate, sodium tungstate, sodium acetate, sodium benzoate, sodium ascorbate, sodium hydrogen carbonate, sodium carbonate and potassium nitrate, and
- wherein said solution has said lubricant completely dissolved in water into a uniform phase in a concentration greater than or equal to one percent by weight, but less than a concentration of a saturated solution.
A method for forming a sintered product from a powder, comprising the steps of:
- applying a solution obtained by dissolving a lubricant in a solvent to a forming portion of a mold body;
- evaporating the solution to form a crystallized layer of the lubricant on a surface of the forming portion;
- filling the forming portion of the mold body with a raw powder, said raw powder being Fe-based metal powder or Cu-based metal powder,
- fitting upper and lower punches into the forming portion;
- pressing the raw powder to form a compact;
- and
- sintering the compact to form a sintered product,
- wherein said lubricant is at least one member selected from the group consisting of dipotassium hydrogen phosphate, disodium hydrogen phosphate, trisodium phosphate, sodium polyphosphate, riboflavin sodium phosphate, potassium sulfate, sodium sulfate, sodium thiosulfate, sodium dodecylsulfate, sodium dodecylbenzenesulfonate, Food Blue No. 1., Food Yellow No. 5., sodium ascorbyl sulfate, sodium tetraborate, sodium silicate, sodium tungstate, sodium acetate, sodium benzoate, sodium ascorbate, sodium hydrogen carbonate, sodium carbonate and potassium nitrate, and
- wherein said solution has said lubricant completely dissolved in water into a uniform phase in a concentration greater than or equal to one percent by weight, but less than a concentration of a saturated solution.
A method for forming a compact from a powder, comprising the steps of:
- applying a solution obtained by dissolving a lubricant in a solvent to a forming portion of a mold body;
- evaporating the solution to form only a crystallized layer of the lubricant on the forming portion;
- filling the forming portion of the mold body with a raw powder, said raw powder being Fe-based metal powder or Cu-based metal powder, and
- then fitting punches into the forming portion,
- wherein said lubricant is at least one member selected from the group consisting of dipotassium hydrogen phosphate, disodium hydrogen phosphate, trisodium phosphate, sodium polyphosphate, riboflavin sodium phosphate, potassium sulfate, sodium sulfate, sodium thiosulfate, sodium dodecylsulfate, sodium dodecylbenzenesulfonate, Food Blue No. 1., Food Yellow No. 5., sodium ascorbyl sulfate, sodium tetraborate, sodium silicate, sodium tungstate, sodium acetate, sodium benzoate, sodium ascorbate, sodium hydrogen carbonate, sodium carbonate and potassium nitrate,
- wherein said lubricant has a solubility of 3 g or more per 100 g water at 20 deg C. in said solution,
- wherein said solution has said lubricant completely dissolved in water into a uniform phase in a concentration greater than or equal to one percent by weight, but less than a concentration of a saturated solution, and
- wherein the solution thus obtained is applied from a spray member to the forming portion in a spraying manner so as to cause the growth of crystal of said lubricant to thereby form said crystallized layer.
A sintered product produced by sintering a compact, said compact being obtained by pressure-forming a Fe-based or Cu-based metal raw powder in a forming portion in a mold, in which a solution obtained by dissolving a lubricant in a solvent is applied to the forming portion of a mold body, and then the solution is evaporated to form only a crystallized layer of the lubricant on the forming portion prior to filling the forming portion of the mold body with said metal raw powder,
- wherein said lubricant is at least one member selected from the group consisting of dipotassium hydrogen phosphate, disodium hydrogen phosphate, trisodium phosphate, sodium polyphosphate, riboflavin sodium phosphate, potassium sulfate, sodium sulfate, sodium thiosulfate, sodium dodecylsulfate, sodium dodecylbenzenesulfonate, Food Blue No. 1., Food Yellow No. 5., sodium ascorbyl sulfate, sodium tetraborate, sodium silicate, sodium tungstate, sodium acetate, sodium benzoate, sodium ascorbate, sodium hydrogen carbonate, sodium carbonate and potassium nitrate,
- wherein said lubricant has a solubility of 3 g or more per 100 g water at 20 deg C. in said solution,
- wherein said solution has said lubricant completely dissolved in water into a uniform phase in a concentration greater than or equal to one percent by weight, but less than a concentration of a saturated solution, and
- wherein the solution thus obtained is applied from a spray member to the forming portion in a spraying manner so as to cause the growth of crystal of said lubricant to thereby form said crystallized layer.
Dependencies are inferred from the claim text.