Ultrahigh-strength steel sheet excellent in hydrogen embrittlement resistance and workability, and manufacturing method therefor

Abstract

The ultrahigh-strength steel sheet contains, in mass %, C: 0.05-0.25%, Si: 1.00-2.5%, Mn: 2.0-4.0%, P: 0.1% or below (not inclusive of 0%), S: 0.05% or below (not inclusive of 0%), Al: 0.01-0.15%, Ti: 0.003-0.10%, N: 0.01% or below (not inclusive of 0%), the balance comprising iron with inevitable impurities, and is a composite structure steel sheet comprising 10-50 area % ferrite and 50 area % or above martensite, in which the average circle-equivalent grain diameter of ferrite grains is 2.0 μm or below, the average aspect ratio of ferrite grains is 2.0 or below, and the tensile strength is 1,100 MPa or above. Accordingly, the ultrahigh-strength steel sheet is excellent in hydrogen embrittlement resistance and workability.