High Toughness Abrasion Resistant Steel with Little Change in Hardness During use and Method of Production of same

Abstract

The present invention provides an abrasion resistant steel having a hardness of HB400 to HB520, having little change of hardness during long term use, and superior in toughness, characterized by containing, by mass %, C: 0.21% to 0.30%, Si: 0.30 to 1.00%, Mn: 0.32 to 0.70%, P: 0.02% or less, S: 0.01% or less, Cr: 0.1 to 2.0%, Mo: 0.1 to 1.0%, B: 0.0003 to 0.0030%, Al: 0.01 to 0.1%, and N: 0.01% or less, further containing one or more of V: 0.01 to 0.1%, Nb: 0.005 to 0.05%, Ti: 0.005 to 0.03%, Ca: 0.0005 to 0.05%, Mg: 0.0005 to 0.05%, and REM: 0.001 to 0.1%, having a balance of Fe, and furthermore having an ingredient with an M value defined by the following formula (1) of −10 to 16: M=26×[Si]−40×[Mn]−3×[Cr]+36×[Mo]+63×[V]  (1)