High strength hot rolled steel plate for spiral line pipe superior in low temperature toughness and method of production of same

Abstract

The present invention provides hot rolled steel plate for spiral pipe superior in low temperature toughness, thick in gauge, for example, having a plate thickness of 14 mm or more, and having a high strength of the API-X65 standard or more spiral pipe and a method of production of the same, that is, steel plate containing, by mass %, C: 0.01 to 0.1%, Si: 0.05 to 0.5%, Mn: 1 to 2%, P≦0.03%, S≦0.005%, O≦0.003%, Al: 0.005 to 0.05%, N: 0.0015 to 0.006%, Nb: 0.005 to 0.08%, Ti: 0.005 to 0.02%, N−14/48×Ti>0%, Nb−93/14×(N−14/48×Ti>0.005%, Mo: 0.01% to less than 0.1%, Cr: 0.01 to 0.3%, and Cu: 0.01 to 0.3%, and having a balance of Fe and unavoidable impurities, characterized in that an elongation rate of a microstructure unit in a cross-section in the pipe circumferential direction after pipemaking is 2 or less.