# US 2009/0260531 A1 · Aluminum alloy plate for lithographic printing plate, lithographic printing plate support, presensitized plate, method of manufacturing aluminum alloy plate for lithographic printing plate and method of manufacturing lithographic printing plate support > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 2009/0260531 A1 - Document ID: US20090260531A1 - Status: Published application - Kind: A1 - Application number: 12/425,836 - Filed: 2009-04-17 - Published: 2009-10-22 - Earliest claimed: 2008-04-18 - Assignees: FUJIFILM Corporation - Inventors: Shinya KUROKAWA; Takanori Mori; Hirokazu Sawada - Web page: https://patentgrep.com/patent/US20090260531A1 ## CPC - B41N 1/083: {made of aluminium or aluminium alloys or having such surface layers (B41N1/086 takes precedence)} - B41N 3/034: {characterised by the electrochemical treatment of the aluminum support, e.g. anodisation, electro-graining; Sealing of the anodised layer; Treatment of the anodic layer with inorganic compounds; Colouring of the anodic layer} - C25F 3/04: of light metals - B41N: PRINTING PLATES OR FOILS (photosensitive material G03); MATERIALS FOR SURFACES USED IN PRINTING MACHINES FOR PRINTING, INKING, DAMPING, OR THE LIKE; PREPARING SUCH SURFACES FOR USE AND CONSERVING THEM - C25F: PROCESSES FOR THE ELECTROLYTIC REMOVAL OF MATERIALS FROM OBJECTS; APPARATUS THEREFOR ## Abstract An aluminum alloy plate for a lithographic printing plate capable of obtaining a lithographic printing plate having an excellent resistance to spotting, a method of manufacturing such aluminum alloy plate, a lithographic printing plate support obtained by using such aluminum alloy plate, and a presensitized plate and in particular an on-machine developable presensitized plate are provided. The aluminum alloy plate contains 0.08 to 0.45 wt % of iron and to 0.20 wt % of silicon, with the balance being inadvertent impurities and aluminum, and the content of aluminum-iron intermetallic compounds is not more than 0.05 wt %. ## Claims ### Claim 1 An aluminum alloy plate for a lithographic printing plate comprising 0.08 to 0.45 wt % of iron and 0.05 to 0.20 wt % of silicon, with the balance being inadvertent impurities and aluminum, wherein aluminum-iron intermetallic compounds are contained in an amount of not more than 0.05 wt %. ### Claim 2 (depends on 1) The aluminum alloy plate for a lithographic printing plate according to claim 1, wherein a main component of intermetallic compounds present in the aluminum alloy plate is α-AlFeSi. ### Claim 3 (depends on 1) The aluminum alloy plate for a lithographic printing plate according to claim 1, wherein a ratio of iron content to silicon content (Fe/Si) in the aluminum alloy plate is from 0.5 to 2.2. ### Claim 4 (depends on 1) The aluminum alloy plate for a lithographic printing plate according to claim 1, wherein zinc is contained in an amount of not more than 0.01 wt %. ### Claim 5 (depends on 1) The aluminum alloy plate for a lithographic printing plate according to claim 1, wherein magnesium is contained in an amount of not more than 0.20 wt %. ### Claim 6 (depends on 1) A method of manufacturing the aluminum alloy plate for a lithographic printing plate according to claim 1, the method comprising: a semicontinuous casting step for forming an ingot from an aluminum alloy melt; a scalping step for scalping the ingot obtained in the semicontinuous casting step; and a soaking step for carrying out a soaking treatment after the scalping step in a temperature range of 500 to 550° C. ### Claim 7 (depends on 1) A method of manufacturing the aluminum alloy plate for a lithographic printing plate according to claim 1, the method comprising: a continuous casting step for rolling an aluminum alloy melt as it is solidified, to thereby form an aluminum alloy plate; a cold rolling step for reducing a thickness of the aluminum alloy plate obtained in the continuous casting step; an intermediate annealing step for heating at a temperature of not more than 500° C. following the cold rolling step; and a finish cold rolling step for reducing a thickness of the aluminum alloy plate following the intermediate annealing step. ### Claim 8 (depends on 1) A lithographic printing plate support obtained by subjecting a surface of the aluminum alloy plate for a lithographic printing plate according to claim 1 to a surface roughening treatment including an electrochemical graining treatment and an anodizing treatment in this order. ### Claim 9 (depends on 8) The lithographic printing plate support according to claim 8, wherein the lithographic printing plate support is obtained by further subjecting the aluminum alloy plate following the anodizing treatment to a hydrophilizing treatment which is a treatment using an alkali metal silicate so that silicon is adsorbed in an amount of 1.0 to 30 mg/m2. ### Claim 10 A method of manufacturing a lithographic printing plate support, the method comprising the steps of: a semicontinuous casting step for forming an ingot from an aluminum alloy melt containing 0.08 to 0.45 wt % of iron and 0.05 to 0.20 wt % of silicon with the balance being inadvertent impurities and aluminum; a scalping step for scalping the ingot formed in the semicontinuous casting step; a hot rolling step for rolling the scalped ingot to obtain a rolled plate; a cold rolling step for reducing a thickness of the rolled plate following the hot rolling step to obtain an aluminum alloy plate; and a surface treatment step in which a surface of the aluminum alloy plate following the cold rolling step is subjected to a surface roughening treatment including an electrochemical graining treatment and an anodizing treatment in this order to obtain the lithographic printing plate support, wherein a thickness (X) of the ingot following the semicontinuous casting step, a plate thickness (Y) following the cold rolling step, an amount (A) of material removed by the scalping step, an amount (B) of material removed by the surface roughening treatment and a thickness (C) of an anodized film satisfy the following expression (i): 4 ≦ Z = X - A Y × ( B + C ) × 10 - 3 + A ≦ 20. ( i ) ### Claim 11 (depends on 10) The method according to claim 10, wherein the thickness (X) of the ingot following the semicontinuous casting step is from 300 to 800 mm, the plate thickness (Y) following the cold rolling step is from 0.1 to 0.5 mm, the amount (A) of material removed by the scalping step is from 1 to 15 mm, the amount (B) of material removed by the surface roughening treatment is from 1 to 10 am, and the thickness (C) of the anodized film is from 0.1 to 2.5 μm. ### Claim 12 (depends on 10) A lithographic printing plate support obtained by the method according to claim 10. ### Claim 13 (depends on 8, 12) A presensitized plate having an image recording layer formed on the lithographic printing plate support according to claim 8 or 12. ### Claim 14 (depends on 13) The presensitized plate according to claim 13, wherein the image recording layer contains anions comprising halide ions and/or PF6−. ### Claim 15 (depends on 13) The presensitized plate according to claim 13, wherein the image recording layer is one in which an image is formed by light exposure and unexposed portions are removable with printing ink and/or fountain solution.