Antibiotic Laminating Film
OwnerAnthony Trajkovich, Lisa Trajkovich +1inventors
InventorsAnthony Trajkovich, Lisa Trajkovich, Don Woodrich
Life of this patent
Estimating the term…
Abstract
An antibiotic film is preferably comprised of a base adhesive layer of Ethylene Vinyl Acetate (EVA), a second layer of Polyethylene Terephthalate (PET), and a final layer of an antibiotic, preferably a zeolite contained in a water-based acrylic coating. The film is applied to a laminate using the inventive method. The laminate may be applied to printed items such as menus, placemats, posters, decontamination materials, and medical documentation.
Claims12
A method of producing a germ resistant advertisement having high quality graphics and having at least one polymer surface, the method comprising the steps of:
- a. providing a water-based dispersion comprising an acrylic and zeolite particles, wherein the zeolite particles have active ions and a particle size of about 6 microns, a pore size of below 3 Angstroms, and comprise from about 0.5% to about 10% by weight of the dispersion,
- b. coating the dispersion onto a surface of an advertisement to create a germ resistant surface, and
- c. drying the dispersion to form a coating layer having an exposed surface containing the zeolite particles.
The method of claim 30, wherein, the dispersion has a viscosity between about 20 centipose and about 1000 centipoise.
The method of claim 30, wherein the zeolite particles comprise from about 0.25% to about 3% by weight of the dispersion.
The method of claim 30, wherein the acrylic particles preferably comprise from about 15% to about 60% by weight of the dispersion.
The method of claim 31, wherein the surface is coated by the dispersion at a rate of about 0.1 lbs./3000 ft. square to 1 lbs./3000 ft. square.
The method of claim 30, wherein the coating layer has a thickness of from about 0.7 microns to about 7 microns.
The method of claim 30, wherein the advertisement is made from the group consisting of cellophanes, vinyl chlorides, vinyl chloride copolymers, cellulose acetate films, vinylidene chlorides, vinylidene chloride copolymers, ethyl cellulose, aluminum foils, methyl cellulose, laminates, polyesters, papers, polyethylenes, paperboards, polypropylenes, glassines, polystyrenes, nylons and combinations thereof.
The method of claim 36, wherein the advertisement further includes a thermal laminating film comprising:
- a base layer of a thermoplastic polymer sheet material having a surface, and a unitary thermal laminating layer disposed on the surface, the unitary thermal laminating layer comprising from about 40% to about 90% by weight of an ethylene vinyl acetate copolymer containing from about 0.1% to about 40% by weight of vinyl acetate units, and
- an amount of an anti-blocking agent effective, when the thermal laminating film is wound on a roll, to prevent the thermal laminating film from sticking to roller surfaces.
A method of generating an antibiotic laminating film comprising:
- providing a dispersion of a zeolite in a water based acrylic coating;
- spreading the dispersion onto a base film layer;
- passing the base film layer with the dispersion coated thereon through an oven to remove all water from the dispersion;
- winding the dried base film layer into a roll;
- extrusion coating the roll with a thermal adhesive;
- corona treating a plain side of the film layer;
- priming the plain side of the film layer to promote adhesion;
- drying the primer;
- extruding adhesive onto the primer side of the film layer;
- cooling the film layer and adhesive to a temperature of about 100 degrees Fahrenheit;
- and
- corona treating the adhesive side of the film.
The method of claim 38, wherein the spreading step comprises coating the acrylic dispersion by a gravure process.
The method of claim 38, wherein the base film layer comprises at least one of the following:
- PET, OPP, nylon, and textured film.
The method of claim 40, further comprising adding at least one of:
- an anti-blocking agent and an ultraviolet absorber.