Antimicrobial Glaze and Acid Resistant Porcelain for Enameled Steel Products
OwnerRam Narayanan, James Michael McHaleinventors
Life of this patent
Estimating the term…
Abstract
The invention provides a cost-effective and practical acid resistant porcelain enamel with antimicrobial properties for steel substrates. The invention provides a porcelain enamel coating which has an optimum range of zinc content and other enamel constituents wherein outstanding antimicrobial performance is achieved without significant degradation of other important properties such as acid resistance.
Claims12
An antimicrobial and acid resistant enamel coating for a steel substrate, comprising:
- an amount of ZnO between 1.0 and 6.0 percent by weight;
- and
- an amount of at least one second substance selected from the group:
- alumina, silica, titania, zirconia, and tin oxide, wherein said amount of said at least one second substance is not less than 1 percent by weight less than the percent by weight amount of ZnO.
An enamel coating for a steel substrate containing a first amount of ZnO, and a second amount of at least one second substance, wherein the enamel coating has an antimicrobial efficacy of 95% or greater as measured in accordance with JIS Z2801 and wherein the enamel coating has at least an “A” rating for acid resistance as measured in accordance with the ASTM C282 Citric Acid Spot Test.
A method of producing an enamel coated porcelain product on a steel substrate comprising:
- preparing a slurry containing a first amount of ZnO, a second amount of a substance selected from the group comprising alumina, silica, titania, zirconia, and tin oxide, and a third amount of glass frit;
- coating a steel substrate with a ground coat enamel;
- spray coating the slurry on top of the ground coat enamel;
- and
- firing the product to form the enamel coated porcelain product.