Fluorine-doped tin oxide transparent conductive film glass and method of fabricating the same

A method of fabricating an FTO transparent conductive film glass used for defogging purposes comprising a glass layer, a dielectric barrier layer, a functional layer, a metal electrode layer, a plastic intermediate layer, and a glass layer, stacked in this sequential order, the method comprising:

• forming a precursor solution by dissolving a tin oxide precursor and a fluorine precursor in deionized water;
• and
• spray-coating the precursor solution on the top surface of the dielectric barrier layer in the temperature range of 400 to 550° C. under air atmosphere, thus forming an FTO transparent conductive film having a molar ratio of F to Sn in the range of 0.5 to 2 and a ratio between a (200) crystal plane and a (301) crystal plane in the range of 1:4 to 1:1 (texture coefficient) as the functional layer.