US 2008/0164628 A1Published application

Method of Manufacturing Anti-Bacteria Polyamide Fiber via High Speed Spinning

AssigneeLiaoning Yinzhu Chemtex Group Co., Ltd.

InventorsXuan DU, Lin ZOU, Xiuying PAN, Lipeng JIANG, Qingfu MENG, Aoxiang HU, Junlong ZHANG, Ke CHEN

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method of manufacturing anti-bacteria polyamide fiber via high speed spinning disclosed a kind of method, which can make manufacturing anti-bacteria polyamide fiber via high-speed spinning realized, including the preparation of anti-bacteria particles and process of high-speed spinning. The preparation of anti-bacteria particles includes surface treatment of anti-bacteria agent and its process of preparation. Choose nano zeolite carrying silver ion as anti-bacteria agent, mix the anti-bacteria particles and polymer chips, after melting, produce anti-bacteria yarns via high speed spinning. The surface treatment to the anti-bacteria agent the invention can improve the spinnability of raw material and place foundation for realizing high speed spinning. Further more, for the spinning pack, adopt good quality mental powder as filtering and pressuring material and increase length diameter rate of hole of spinneret to lengthen the friction distance that the melt passing the spinneret holes in order to eliminate the inner energy of polymer, which prevent the melt from breaking cause by released inner energy while polymer bursting from the spinneret holes. The method described in the invention is simple and easy to implemented. High speed spinning realized by adopting this method, solve the problems of long process rout, low output and lower grade products caused by existing low-speed spinning and greatly increase the beneficial result of enterprise.

Claims3

Dependent claims

A method of manufacturing anti-bacteria polyamide fiber via high speed spinning, is to mix the polyamide particle with anti-bacteria agent and polymer chips, and melt, then, produce anti-bacteria polyamide fiber via high speed spinning, characterized in that:

Preparation of Anti-bacteria Particles
To choose high-grade anti-bacteria agent that is nano inorganic salts carrying silver ion, that is zeolite carries silver ion with particle diameter of 20-80 nm;
The formula of water solution of surface treatment agent of anti-bacteria agent:
Component
Proportion by Weight (unit:
kg)
Methylphenyl silicone oil
8.0-12.0
Dodecyl sodium sulfate
0.5-2.0
Water
85-95
Method of Treatment:
Mix and pickle the water solution of treatment agent and anti-bacteria agent with the proportion of 100:5-8 by weight, heat up to 80°, the pickling time is 30-60 min and then, filter and dry;
The preparation process of anti-bacteria particles:
Put the surface treated anti-bacteria agent and PA chips with the weight proportion of 20-30:70-80 into double screw extruder to be melted and granulated under blending, and make anti-bacteria PA chip particle out with anti-bacteria particle;
The blending granulation temperature of PA 6 anti-bacteria particle is 265-270□, the blending granulation temperature of PA66 anti-bacteria particle is 290-300□;
High Speed of Anti-bacteria PA Fibers:
Prepare polyamide chip and anti-bacteria particle with the proportion of 9-10:1 by weight and mix the two materials by blender, then, put into dryer, and after blending and melting through screw extruder, spin under high speed via spinning pack, and then cool by air, cluster and finish under 3,900-4,300 m/min, and make out anti-bacteria PA POY

16 more elements