655 Mpa Grade Martensitic Stainless Steel Having High Toughness and Method for Manufacturing the Same

Abstract

A martensitic stainless steel for inexpensive seamless pipe having 655 MPa yield strength, high toughness and excellent corrosion resistance in high CO2 environments, and a method for manufacturing thereof is provided. The steel comprises C:0.005-0.05%, Si:0.1-0.5%, Mn: 0.1-2.0% P: −0.005%, S: −0.005%, Cr: 10.0-12.5%, Mo: 0.1-0.5%, Ni: 1.5-3.0%, N: −0.02%, Al: 0.01-0.1%, by weight, while FI value defined by the formula [FI=Cr+Mo−Ni−30 (C+N)] being 5.00 to 8.49, and balance of substantially Fe. The method comprises the steps of reheating the cooled steel at temperatures from 780° C. to 960° C., quenching the reheated steel, and then tempering the quenched steel at temperatures from 550° C. to 650° C.