Water-gas shift and reforming catalyst and method of reforming alcohol
OwnerTodd Healey, Peter DeVriesinventors
Life of this patent
Estimating the term…
Abstract
A supported catalyst for reforming alcohol, particularly for steam reforming methanol, to produce hydrogen for use in fuel cells includes a ceramic support and a catalyst coated thereon. The catalyst contains at least one platinum group metal such as platinum, iridium, rhenium, palladium, or osmium, and where the at least one platinum group metal is reduced, and is also coated with a lanthanide group metal or metal oxide. Preferably, the catalyst contains at least 0.05% by weight of at least one platinum group metal, at least 0.05% by weight of an at least one metal or metal oxide of cerium or lanthanum, and at least 0.05% by weight of an at least one metal or metal oxide of chromium, manganese, or iron.
Claims15
A supported catalyst, comprising a support and a catalyst residing on said support, the catalyst comprising at least one platinum group metal selected from the group consisting of platinum, iridium, rhenium, palladium, ruthenium and osmium, and where the at least one platinum group metal is reduced, and coated with a second metal or metal oxide.
A supported catalyst for methanol steam reforming or for water-gas shift reactions, comprising a catalyst residing on a support, and the catalyst comprises at least one platinum group metal selected from the group consisting of platinum, iridium, rhenium, palladium, ruthenium, and osmium, and at least one metal or metal oxide of cerium or lanthanum, and at least one metal or metal oxide of chromium, manganese, or iron.
A method for reforming alcohol, comprising the steps of providing a supported catalyst, said catalyst residing on said support and the catalyst comprising at least one platinum group metal selected from the group consisting of platinum, iridium, rhenium, palladium, ruthenium, and osmium, and where the at least one platinum group metal is reduced, and coated with a lanthanide metal or metal oxide, which further contains at least one of chromium, manganese, or iron, or oxides thereof, in the coating over said reduced platinum group metals;
- heating the catalyst to a temperature between 200° C. and 900° C.;
- and feeding a heated alcohol and water mixture to the catalyst such that products of at least hydrogen and carbon dioxide are formed.
A method for steam reforming methanol, comprising the steps of providing a supported catalyst, said catalyst residing on said support and the catalyst comprising at least one platinum group metal selected from the group consisting of platinum, iridium, rhenium, palladium, ruthenium, and osmium, and where the at least one platinum group metal is reduced, and coated with a metal or metal oxide of at least one of cerium, lanthanum, or zinc which further contains at least one of chromium, manganese, or iron, or oxides thereof, in the coating over said reduced platinum group metal;
- heating the catalyst to a temperature between 150° C. and 700° C.;
- and feeding a heated methanol and steam mixture to the catalyst such that products of at least hydrogen and carbon dioxide are formed.
A method for performing a water-gas shift reaction with a catalyst, comprising the steps of providing a supported catalyst, said catalyst residing on said support and the catalyst comprising at least one platinum group metal selected from the group consisting of platinum, iridium, rhenium, palladium, ruthenium, and osmium, and where the at least one platinum group metal is reduced, and coated with a metal or metal oxide of at least one of cerium, lanthanum, chromium, manganese, zinc or iron;
- heating the catalyst to a temperature between 150° C. and 700° C.;
- and feeding a gas containing carbon monoxide and steam to the catalyst such that products of at least hydrogen and carbon dioxide are formed.
A method of making a supported catalyst comprising the steps of depositing platinum onto a support by contacting said support with a liquid solution containing platinum;
- drying the support;
- reducing the platinum residing on said support;
- depositing cerium, lanthanum or zinc onto the reduced supported platinum by contacting the reduced supported platinum with a solution containing cerium, lanthanum, or zinc;
- and drying the support with the reduced platinum and cerium, lanthanum or zinc thereon.
A catalyst for methanol steam reforming, comprising at least 0.05% by weight of a platinum group metal selected from the group consisting of platinum, iridium, rhenium, palladium, ruthenium, and osmium;
- at least 0.05% by weight of at least one metal or metal oxide of cerium, lanthanum, or zinc;
- and at least 0.05% by weight of at least one metal or metal oxide of chromium, manganese, or iron.
Dependencies are inferred from the claim text.