Surface modification method for conductive metal material
AssigneeJapan Aviation Electronics Industry, Limited
InventorsRyoji Kaku, Masafumi Okada
Life of this patent
Estimating the term…
Abstract
Spherical particles having curvatures larger than those of irregularities, crystal grain boundaries, lattice defects or the like (referred to collectively as irregularities, hereinafter) on the surface of a conductive metal material are ejected at high speeds to make the particles collide against the surface of the conductive metal material, thereby repeatedly causing rapid melting and cooling at the minute points of impact of the particles, thereby changing the surface into amorphous. Then, spherical particles having curvatures smaller than those of irregularities on the surface subjected to the treatment described above collide against the surface, thereby changing the surface into amorphous and planarizing the surface.
Claims5
A surface modification method for a conductive metal material, comprising:
- a first modification step of bombarding the conductive metal material with spherical particles, each of which is made of a material that does not crack if the particle collides against the conductive metal material and has a curvature approximately equal to or more than curvatures of irregularities on the surface of the conductive metal material;
- and
- a second modification step of bombarding the surface of the conductive metal material treated in the first modification step with spherical particles, each of which is made of a material that does not crack if the particle collides against the conductive metal material and has a curvature less than curvatures of irregularities on the surface of the conductive metal material treated in the first modification step.
A conductive metal material, wherein an amorphous layer having a thickness of at least 10 Å is formed at the surface of the conductive metal material,
- the size of crystal grains of the conductive metal material under the amorphous layer decreases as the distance from the amorphous layer decreases, and
- the surface of the amorphous layer is planarized compared with a surface having irregularities that become a starting point of corrosion.
Dependencies are inferred from the claim text.