Tin-plated product and method for producing same

Abstract

A tin-plated product formed by electroplating a substrate in a tin plating solution, which contains carbon particles and an aromatic carbonyl compound, to form a coating of a composite material, which contains the carbon particles in a tin layer, on the substrate has a coefficient of friction which is not greater than 0.18, preferably not greater than 0.13, with respect to the same kind of another tin-plated product, and has a glossiness of not less than 0.29 and a contact resistance of not greater than 1.0 mΩ. The coating has a thickness of 0.5 to 10 micrometers, and the content of carbon in the coating is in the range of from 0.1% by weight to 1.5% by weight. Separate protrusions containing the carbon particles are formed on the surface of the coating. The orientation plane of a tin matrix of the coating is (101) plane.