Epoxy-acrylate/amine adhesive composition

A 2 part film coating or laminating adhesive composition made up of parts A and B and having a viscosity of from 10 to 2000 cps at 25° C. wherein part A comprises a mixture of epoxy resin and a polymethacrylate ester and part B comprises a polyoxyalkylenepolyamine, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition made up of parts A and B and having a viscosity of from 10 to 2000 cps at 25° C., wherein part A comprises a mixture of epoxy resin and a polyacrylate ester and part B is chosen from the group consisting of polyoxypropylenepolyamine, bis-(3-aminopropoxy)-polyoxyethyl ether and a mixture of polyoxypropylenepolyamines and bis-(3-aminopropoxy)-polyoxyethyl ethers and bis-(3-aminopropoxy)-diethyl ether and bis-(2-aminopropoxy)-diisopropyl ether.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of a mixture of epoxy resin and a polyacrylate ester and part B comprises a polyoxyalkylenepolyamine or a mixture of polyoxyalkylenepolyamine and an adduct obtained from a reaction of a polyoxyalkylenepolyamine and a mono or polyglycidyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol A and trimethylolpropane triacrylate and part B is bis-(3-aminopropoxy)-diethyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol F and trimethylolpropane triacrylate and part B is bis-(3-aminopropoxy)-diethyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol A, trimethylolpropane triacrylate and tripropylene glycol diacrylate and part B is bis-(3-aminopropoxy)-diethyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol F, trimethylolpropane triacrylate and tripropylene glycol diacrylate and part B is bis-(3-aminopropoxy)-diethyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol A and trimethylolpropane triacrylate and part B is bis-(2-aminopropoxy)-diisopropyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol F and trimethylolpropane triacrylate and part B is bis-(2-aminopropoxy)-diisopropyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol A, trimethylolpropane triacrylate and tripropylene glycol diacrylate and part B is bis-(2-aminopropoxy)-diisopropyl ether, parts A and B being mixed together to form said composition.

A 2 part film coating or laminating adhesive composition having a viscosity of from 10 to 2000 cps at 25° C. wherein part A is comprised of epoxy resin of Bis phenol F, trimethylolpropane triacrylate and tripropylene glycol diacrylate and part B is bis-(2-aminopropoxy)-diisopropyl ether, parts A and B being mixed together to form said composition.