Polymeric blends that adhere to polycarbonates and polycarbonate alloys
OwnerPurushottam Das Agrawal, Marvin C. Hill +1inventors
InventorsPurushottam Das Agrawal, Marvin C. Hill, Kelly Kirkendall
Life of this patent
Estimating the term…
Abstract
The invention relates to polymeric blends comprising at least about 40 percent by weight thermoplastic polyurethane elastomer; and from about 10 to about 250 parts by weight ethylene vinyl acetate copolymer per 100 parts by weight thermoplastic polyurethane elastomer. These blends exhibit high adhesion to polycarbonates and polycarbonate alloys.
Claims4
A polymeric blend comprising:
- at least about 40 percent by weight thermoplastic polyurethane elastomer;
- and
- from about 10 to about 250 parts by weight ethylene vinyl acetate copolymer per 100 parts by weight thermoplastic polyurethane elastomer.
A polymeric blend comprising:
- at least about 40 percent by weight thermoplastic polyurethane elastomer;
- from about 10 to about 250 parts by weight ethylene vinyl acetate copolymer per 100 parts by weight thermoplastic polyurethane elastomer;
- and
- from about 10 to about 60 parts by weight polypropylene per 100 parts by weight thermoplastic polyurethane elastomer.
1 more element
A polymeric blend comprising:
- from about 48 to about 52 percent by weight thermoplastic polyurethane elastomer;
- from about 18 to about 22 percent by weight ethylene vinyl acetate copolymer;
- from about 13 to about 17 percent by weight thermoplastic vulcanizate comprising a blend of polypropylene and EPDM;
- from about 8 to about 12 percent polypropylene homopolymer;
- and
- from about 3 to about 7 percent maleated polypropylene.
3 more elements
A polymeric blend comprising:
- from about 58 to about 62 percent by weight thermoplastic polyurethane elastomer;
- from about 13 to about 17 percent by weight ethylene vinyl acetate copolymer;
- from about 13 to about 17 percent by weight thermoplastic vulcanizate comprising a blend of polypropylene and EPDM;
- from about 3 to about 7 percent polypropylene homopolymer;
- and
- from about 3 to about 7 percent maleated polypropylene.
3 more elements