Polymeric compositions
OwnerLuc Moens, Kris Buysens +1inventors
InventorsLuc Moens, Kris Buysens, Daniel Maetens
Life of this patent
Estimating the term…
Abstract
There is described a radiation curable powder composition which comprisesa) 10 to 90% weight of an ethylenically unsaturated polyester and/or acrylic copolymer having an “in chain” unsaturation from 0.35 to 3.50 milliequivalents of double bonds per gram resinb) 10 to 90% weight of an ethylenically unsaturated (hydrogenated) polyphenoxy resin having a vinyl group, an allyl group, a(meth)acrylate ester group or a diacid or anhydride containing unsaturated groups; andc) 0 to 30% weight of an ethylenically unsaturated oligomer.
Claims21
A radiation-curable powder composition which comprises:
- a) a first component comprising from about 10% to about to 90% by weight of an ethylenically unsaturated telechelic polyester and/or acrylic telechelic copolymer;
- b) a second component comprising from about 10% to about [90%] by weight of an ethylenically unsaturated non aromatic polyoxy resin;
- and c) optionally a third component comprising up to about 30% by weight of an ethylenically unsaturated polymer precursor.
A radiation-curable powder composition which comprises a) a first component comprising from about 10% to about to 90% by weight an ethylenically unsaturated polyester and/or acrylic [COPOLYMER HAVING AN “IN] chain” unsaturation from 0.35 to 3.50 milliequivalents of double bonds per gram;
- b) a second component comprising from about 10% to about to 90% by weight of an ethylenically unsaturated (hydrogenated) polyphenoxy resin comprising a vinyl group, an allyl group, a (meth)acrylate ester group or a diacid or anhydride containing unsaturated groups;
- c) a third component from about 0 to about 30% by weight of an ethylenically unsaturated oligomer.
A composition according to either preceding claim, in which the first component comprising an ethylenically unsaturated polyester obtained and/or obtainable by reacting (i) an acid component comprising from 50 to 95% mole of an aliphatic, cycloaliphatic or aromatic polyacid and from 5 to 50% mole of an unsaturated polyacid;
- with (ii) an alcohol component comprising an aliphatic and/or cycloaliphatic polyol.
A composition according to any preceding claim, in which the first component comprises an ethylenically unsaturated polyester having hydroxyl and/or carboxylic acid end groups.
A composition according to any of the preceding claim, where the first component is obtained and/or obtainable by reacting:
- (a) a diisocyanate;
- a hydroxyalkyl(meth)acrylate and an ethylenically unsaturated polyester;
- or (b) a glycidyl(meth)acrylate and an ethylenically unsaturated polyester.
A composition according to any preceding claim, in which the first component comprises an ethylenically unsaturated polyester with a degree of telechelic unsaturation from about 0 to about 2 milliequivalents of double bonds per gram of polyester.
A composition according to any preceding claim, in which the first component comprises an ethylenically unsaturated acrylic copolymer obtained and/or obtainable by reacting:
- (a) an acrylic copolymer comprising functional groups obtained and/or obtainable from (i) from about 40 to about 95 mole % of at least one monomer having acrylic or methacrylic groups, (ii) optionally up to about 60 mole % of another ethylenically unsaturated monomer;
- and (iii) from about 5 to about 60 mole % of an ethylenically unsaturated monomer having a functional group capable of reacting with one or more:
- epoxy, carboxylic acid, hydroxy and/or isocyanate.
- (b) a monomer having an ethylenically unsaturated group and a functional group capable of reacting with one or more:
- epoxy;
- carboxylic acid, hydroxy and/or isocyanate.
A composition according to any preceding claim, in which the first component comprises an ethylenically unsaturated acrylic copolymer characterised by at least one of the following properties and any combinations thereof:
- [(I) ] a number averaged molecular weight from about 1000 to about 8000 (preferably from about 2,000 to about 6,000) daltons;
- (II) a glass transition temperature from about 45 to about [100° C.];
- (III) a degree of unsaturation from about 0.35 to about 3.50 (preferably from about 0.5 to about 2.5) milliequivalents of double bonds per gram of acrylic copolymer;
- and/or [(III)] a melt viscosity (measured by the cone plate method at [200° C.)] of less than about 50,000 [MPA.] s.
A composition according to any preceding claim, in which the first component comprises an acrylic copolymer and the third component comprises an ethylenically unsaturated monomer comprising at least one:
- (meth)acrylate ester group, allyl group, vinyl group, unsaturated diacid and/or unsaturated anhydride, the monomer being capable of reacting with at least one carboxylic acid, epoxy, isocyanate and/or hydroxyl group of the acrylic copolymer.
A composition according to any preceding claim, in which the second component is obtained and/or obtainable by reacting (a) a (hydrogenated) polyphenoxy resin comprising at least one glycidyl group with (b) the reaction product [OF:] (i) an alcohol comprising a vinyl or allyl group;
- with an anhydride;
- (ii) a hydroxyalkyl(meth)acrylate with an anhydride;
- [AND/OR] (iii) an allyl or vinyl glycidyl ether with a polyacid;
- a mono or polyfunctional unsaturated carboxylic acid and/or anhydrides thereof.
A composition according to any preceding claim, in which the second component is characterised by at least one of the following properties and any combinations thereof:
- [(1)] a number averaged molecular weight from about 450 to about 5000 (preferably from about 650 to about 3500);
- (II) a glass transition temperature from about 30 to about [80° C.] (III) a degree of unsaturation from about 0.2 to about 6.0, (preferably from about 0.5 to about 4.5) milliequivalents of double bonds per gram of resin;
- and/or [(IV) A] melt viscosity (measured by the cone plate method at [200° C.)] of less than about 20,000 [MPA.] s.
A composition according to any preceding claim, in which the third component comprises an oligomer comprising at least one functional group selected from a (meth)acrylate ester group, an allyl group, a vinyl group, an unsaturated diacid and/or an unsaturated anhydride.
A radiation curable powder composition which additionally comprises up to about 15 (preferably up to about 8) parts by weight of a photo-initiator for every 100 parts by weight of (as a binder) a composition according to any preceding claim.
A radiation curable powder composition which additionally comprises up to about 10 parts by weight of at least one substance which is effective in modifying coating properties for every 100 parts by weight of (as a binder) a composition according to any preceding claim.
A powder varnish and/or powder paint comprising a radiation curable powder composition according to any preceding claim.
A process for coating an article with a composition as claimed in any preceding claim which comprises the steps of (a) depositing the composition on the article (b) melting the coating thus obtained;
- and (c) exposing the molten coating to radiation sufficient to form a cured coating.
Dependencies are inferred from the claim text.