Process for the recovery of palladium from spent silica
AssigneeCouncil of Scientific and Industrial Research
InventorsArvindkumar Balvantrai Boricha, Hari Chand Bajaj, Raksh Vir Jasra, Pradyut Ghosh, Pushipito Kumar Ghosh
Life of this patent
Estimating the term…
Abstract
The present invention provides a provides a process for the recovery of precious metals from spent catalysts or adsorbent or inorganic waste, more specifically the process relates to recovery of Pd from silica, which is used as an adsorbent in column chromatography or as a catalyst support in many catalysts.
Claims16
) A process for the recovery of palladium as its salt from palladium complex adsorbed on spent silica gel, said process comprising steps of:
- a) burning the spent silica gel with palladium complex adsorbed on its surface, in a furnace in the temperature range of 300-700° C. in presence of air for a period ranging between 2 and 8 hours to oxidize the organic compound in the complex;
- b) cooling the burnt residue of step (a), digesting with a mineral acid at a temperature range of 70-100° C. for a time period of 1-6 hours;
- c) cooling the solution of step (b) to an ambient temperature;
- d) filtering the cooled solution of step (c) to obtain a filtrate and a residue;
- e) washing the residue of step (d) with a mineral acid and drying at 60-100° C. to recover silica;
- f) adjusting the pH of the filtrate of step (d) to obtain a precipitate, filtering to remove the precipitate;
- and
- g) further raising the pH of the filtrate obtained in step (f) to obtain a palladium salt.
) A process as claimed in claim 1, wherein in step (a), the palladium complex is burnt preferably in the temperature range of 350-450° C. and more preferably in the range of 350-400° C.
) A process as claimed in claim 1, wherein in step (b) the concentration of mineral acid used is in the range of 2-3 molar hydrochloric acid.
) A process as claimed in claim 1, wherein in step (d), the original structural properties namely surface area and pore volumes are maintained in the recovered silica.
) A process as claimed in claim 1, wherein in step (d), the recovered silica is reusable.
) A process as claimed in claim 1, wherein in step (d), the mineral acid used to wash the residue is 0.5-M hydrochloric acid.
) A process as claimed in claim 1, wherein in step (d), the pH of the filtrate is adjusted to about 6.0.
) A process as claimed in claim 1, wherein in step (f), the pH of the filtrate is adjusted in the range of 8.5-9.3, preferably pH 9.3.
) A process as claimed in claim 1, wherein in step (g), the purity of palladium salt obtained is about 97-100%.
) A process as claimed in claim 1, wherein the percentage yield of the palladium salt recovered in step (d) is in the range of about 95-100%.
) A process for the recovery of palladium as its salt from palladium phthalocyanine complex adsorbed on spent silica gel, the said process comprising steps of:
- a) treating spent silica containing organic material with hydrofluoric acid;
- b) filtering the solution of step (a) to obtain a solution containing H2SiF6 and suspended palladium phthalocyanine complex;
- c) recovering palladium phthalocyanine complex of step (b) by gravity separation, digesting it by refluxing with an aqueous mineral acid for a time period of 2-4 hours;
- d) filtering the digested mixture of step (c) to remove phthalocyanine to obtain aqueous acidic filtrate solution;
- e) recovering palladium as its salt of the mineral acid by evaporation of the aqueous acidic filtrate solution of step (d);
- and
- f) recovering phthalocyanine ligands by solvent extraction.
) A process as claimed in claim 11, wherein in step (c) the concentration of mineral acid used is in the range of 2-3 molar hydrochloric acid.
) A process as claimed in claim 11, wherein in step (e) the mineral acid used is 5-10 molar hydrochloric acid.
) A process as claimed in claim 11, wherein in step (f) the solvent used is preferably chloroform.
) A process as claimed in claim 11, wherein in step (b) the spent silica is recovered as a value added product namely H2SiF6.
) A process as claimed in claim 11, wherein the solvent used in step (f) is reusable.