Oxidation and fatigue resistant metallic coating
AssigneeUnited Technologies Corporation
InventorsRussell Albert Beers, Allan A. Noetzel, Abdus Khan
Life of this patent
Estimating the term…
Abstract
The present invention relates to a metallic coating to be deposited on gas turbine engine components. The metallic coating comprises up to 18 wt % cobalt, 3.0 to 18 wt % chromium, 5.0 to 15 wt % aluminum, 0.1 to 1.0 wt % yttrium, up to 0.6 wt % hafnium, up to 0.3 wt % silicon, 3.0 to 10 wt % tantalum, up to 9.0 wt % tungsten, 1.0 to 6.0 wt % rhenium, up to 10 wt % molybdenum, and the balance nickel.
Claims67
A metallic coating for providing oxidation and fatigue resistance having a composition comprising up to 18 wt % cobalt, 3.0 to 18 wt % chromium, 5.0 to 15 wt % aluminum, 0.1 to 1.0 wt % yttrium, up to 0.6 wt % hafnium, up to 0.3 wt % silicon, 3.0 to 10 wt % tantalum, up to 9.0 wt % tungsten, 1.0 to 6.0 wt % rhenium, up to 10 wt % molybdenum, and the balance nickel.
A metallic coating having a composition consisting essentially of up to 15 wt % cobalt, 5.0 to 18 wt % chromium, 5.0 to 12 wt % aluminum, 0.1 to 1.0 wt % yttrium, up to 0.06 hafnium, up to 0.3 wt % silicon, 3.0 to 10 wt % tantalum, up to 5.0 wt % tungsten, 1.0 to 6.0 wt % rhenium, up to 10 wt % molybdenum, and the balance nickel.
A metallic coating consisting essentially of up to 2.0 wt % cobalt, 10 to 15 wt % chromium, 6.0 to 10 wt % aluminum, 0.2 to 0.7 wt % yttrium, 0.2 to 0.6 hafnium, 0.001 to 0.1 wt % silicon, 5.0 to 7.0 wt % tantalum, 1.0 to 4.0 wt % tungsten, 1.0 to 3.5 wt % rhenium, up to 4.0% molybdenum, and the balance nickel.
A metallic coating consisting of 12.5 wt % chromium, 8.0 wt % aluminum, 0.4 to 0.7 wt % yttrium, 0.4 wt % hafnium, 6.0 wt % tantalum, 2.0 wt % tungsten, 2.0 wt % rhenium, and the balance nickel.
A metallic coating consisting essentially of 2.0 to 18 wt % cobalt, 3.0 to 10 wt % chromium, 5.5 to 15 wt % aluminum, 0.1 to 1.0 wt % yttrium, up to 0.6 wt % hafnium, up to 0.3 wt % silicon, 3.0 to 10 wt % tantalum, 1.0 to 9.0 wt % tungsten, 1.0 to 5.0 wt % rhenium, 0.2 to 4.0 wt % molybdenum, and the balance nickel.
A metallic coating having a composition consisting essentially of 8.0 to 12 wt % cobalt, 4.0 to 6.5 wt % chromium, 7.5 to 12.5 wt % aluminum, 0.2 to 0.7 wt % yttrium, 0.2 to 0.6 wt % hafnium, up to 0.3 wt % silicon, 5.0 to 7.0 wt % tantalum, 4.2 to 5.8 wt % tungsten, 2.3 to 3.7 wt % rhenium, 1.4 to 2.0 wt % molybdenum, and the balance nickel.
A metallic coating consisting of 10.5 wt % cobalt, 5.0 wt % chromium, 9.0 wt % aluminum, 0.4 to 0.7 wt % yttrium, 04 wt % hafnium, 0.1 wt % silicon, 6.0 wt % tantalum, 5.0 wt % tungsten, 3.0 wt % rhenium, 1.7 wt % molybdenum, and the balance nickel.
A method for depositing an overlay coating on a substrate comprising:
- providing a substrate material formed from at least one of a nickel-based, a cobalt-based, and an iron-based metallic material;
- and
- depositing onto said substrate a coating having a composition consisting essentially of up to 18 wt % cobalt, 3.0 to 18 wt % chromium, 5.0 to 15 wt % aluminum, 0.1 to 1.0 wt % yttrium, up to 0.6 wt % hafnium, up to 0.3 wt % silicon, 3.0 to 10 wt % tantalum, up to 9.0 wt % tungsten, 1.0 to 6.0 wt % rhenium, up to 10 wt % molybdenum, and the balance nickel.
Dependencies are inferred from the claim text.