Transparent conductive laminate and process of producing the same

Abstract

A transparent conductive laminate having a completely crystallized, transparent conductive layer on a substrate comprising an organic polymer molding, and a process for producing the same. The transparent conductive layer is excellent in transparency and wet heat confidence and is not excessively low in specific resistivity. The transparent conductive laminate includes a substrate comprising an organic polymer molding having formed thereon a completely crystallized, transparent conductive layer comprising an In.Sn composite oxide having an amount of Sn atom of 1 to 6% by weight based on the total weight of In atom and Sn atom and having a film thickness of 15 to 50 nm, a Hall mobility of 30 to 45 cm2/V·S, and a carrier density of from 2×1020/cm3 to 6×1020/cm3.