Biaxially oriented, laminated polyester film
AssigneeToray Industries, Inc.
InventorsJun Kobayashi, Eiji Doi, Masanobu Dobuchi
Life of this patent
Estimating the term…
Abstract
A biaxially oriented, laminated polyester film having at least two layers, and in the film, an irregularity in film thickness determined within 4 mm width at an arbitrary position in a transverse direction of the film is about 0.1 μm or less. This polyester film can satisfy both the electromagnetic conversion property and the running ability at a high level, particularly when the film is used as a base film for a large capacity tape for data storage.
Claims11
A biaxially oriented, laminated polyester film having at least two layers, wherein an irregularity in film thickness determined within 4 mm width at an arbitrary position in a transverse direction of said film is about 0.1 μm or less.
A biaxially oriented, laminated polyester film having at least two layers, wherein:
- an irregularity in film thickness determined within 4 mm width at an arbitrary position in a transverse direction of said film is about 0.1 μm or less;
- a first protrusion-height distribution indicating a relationship between heights of protrusions (HA [nm]) and numbers of protrusions at respective protrusion heights (YA [number/mm2]) on a surface of one surface layer (A) satisfies equation (1), and a second protrusion-height distribution indicating a relationship between heights of protrusions (HB [nm]) and numbers of protrusions at respective protrusion heights (YB [number/mm2]) on a surface of another surface layer (B) satisfies equation (2):
- −0.12×HA+4≦log10YA≦−0.07≦HA+5 (1) −0.033×HB+4≦log10YB≦−0.0125×HB+5 (2);
- inert particles I having a mean primary particle diameter of about 0.02 to about 0.15 μm are contained in said surface layer (A) at a content of about 0.001 to about 0.25 wt %, based on the weight of the film;
- and
- at least two kinds of inert particles II and III having mean particle diameters different from each other are contained in said surface layer (B), the mean particle diameter of said inert particles II is in a range of about 0.1 to about 0.4 μm and the content thereof is in a range of about 0.1 to about 0.4 wt %, based on the weight of the film, and the mean particle diameter of said inert particles III is greater than that of said inert particles II and is in a range of about 0.3 to about 1.0 μm and the content thereof is in a range of about 0.002 to about 0.1 wt %, based on the weight of the film.
A biaxially oriented, laminated polyester film having at least two layers, wherein:
- an irregularity in film thickness determined within 4 mm width at an arbitrary position in a transverse direction of said film is about 0.1 μm or less;
- a first protrusion-height distribution indicating a relationship between heights of protrusions (HA [nm]) and numbers of protrusions at respective protrusion heights (YA [number/mm2]) on a surface of one surface layer (A) satisfies equation (1), and a second protrusion-height distribution indicating a relationship between heights of protrusions (HB [nm]) and numbers of protrusions at respective protrusion heights (YB [number/mm2]) on a surface of another surface layer (B) satisfies equation (2):
- −0.12×HA+4≦log10YA≦−0.07×HA+5 (1) −0.033×HB+4≦log10YB≦−0.0125×HB+5 (2);
- inert particles I having a mean primary particle diameter of about 0.02 to about 0.15 μm are contained in said surface layer (A) at a content of about 0.001 to about 0.25 wt %, based on the weight of the film;
- and
- at least two kinds of inert particles II and III having mean particle diameters different from each other are contained in said surface layer (B), the mean particle diameter of said inert particles II is in a range of about 0.1 to about 0.4 μm and the content thereof is in a range of about 0.1 to about 0.4 wt %, based on the weight of the film, and the mean particle diameter of said inert particles III is greater than that of said inert particles II and is in a range of about 0.3 to about 1.0 μm and the content thereof is in a range of about 0.002 to about 0.1 wt %, based on the weight of the film,
- wherein Young's moduli in longitudinal and transverse directions of said film are in a range of about 3,500 to about 10,000 MPa, respectively, and the ratio of both Young's moduli (longitudinal/transverse) is in a range of about 1.0 to about 2.5, and
- wherein on the surface of said surface layer (A), the number of large protrusions having a height of more than 0.270 μm is about {fraction (100/100)} cm2 or less, the number of large protrusions having a height of more than 0.540 μm is about {fraction (2/100)} cm or less, and the number of large protrusions having a height of more than 0.810 μm is about to. {fraction (1/100)} cm2.