US 2003/0143320 A1Published application
Light diffuser fabrication method
AssigneeCheng-Chung LEE
InventorsCheng-Chung Lee, Jin-Cherng Hsu
Life of this patent
Estimating the term…
Abstract
A light diffuser fabrication method includes the step of (a) selecting sands for blasting subject to the size of spot light source and number of pixels of the display to be used, (b) sand blasting a glass substrate with selected sands to form a multi-frequency refracting substrate, (c) coating the multi-frequency refracting substrate with polysiloxane by bathing, (d) baking the polysilixane coated multi-frequency refracting substrate into the desired light diffuser.
Claims2
A light diffuser fabrication method comprising the steps of:
- (a) selecting the sizes of sands subject to the number of light spots per inch counted subject to the size of spot light source and number of pixels of the display to be used;
- (b) preparing a glass substrate and then blasting the selected sands onto the surface of the glass substrate to form a multi-frequency refracting substrate of refracting power within about 1.56˜1.58 under wavelength 550 nm;
- (c) dipping the multi-frequency refracting substrate thus obtained in polysiloxane solution in a bath at temperature within about 5° C.˜18° C., for enabling the multi-frequency refracting substrate to be covered with a layer of polysiloxane;
- and
- (d) baking the polysilixane coated multi-frequency refracting substrate thus obtained at 80° C. for about 90 minutes, and then backing the polysilixane coated multi-frequency refracting substrate at 125° C. for about 15 minutes, causing the polysilixane coating to be curled and formed into a layer of oxidized silicon coating of chemical bond —O—Si—O—Si—O— and of refracting power within about 1.47˜1.5 under wavelength 550 nm on the multi-frequency refracting substrate
2 more elements
The light diffuser fabrication method comprising the steps of:
- (a) selecting the sizes of sands subject to the number of light spots per inch counted subject to the size of spot light source and number of pixels of the display to be used;
- (b) preparing a mold having a cavity, and then sand-blasting the surface of the cavity of the mold, and then using the mold to produce a desired multi-frequency refracting substrate of refracting power within about 1.56˜1.58 under wavelength 550 nm;
- (c) dipping the multi-frequency refracting substrate thus obtained in polysiloxane solution in a bath at temperature within about 5° C.˜18° C., for enabling the multi-frequency refracting substrate to be covered with a layer of polysiloxane;
- and
- (d) baking the polysilixane coated multi-frequency refracting substrate thus obtained at 80° C. for about 90 minutes, and then backing the polysilixane coated multi-frequency refracting substrate at 125° C. for about 15 minutes, causing the polysilixane coating to be curled and formed into a layer of oxidized silicon coating of chemical bond —O—Si—O—Si—O— and of refracting power within about 1.47˜1.5 under wavelength 550 nm on the multi-frequency refracting substrate
2 more elements
Dependencies are inferred from the claim text.