Loading patent…
AssigneeHowmet Research Corporation
InventorsJoseph M. Vihtelic, Alan J. Graham, Robert L. McCormick, Laura A. Carpenter
Estimating the term…
An investment casting method using a pattern material with substantially spherical filler particulates is used to produce investment cast components with iproved surface quality, reduced finishing costs, and reduced core breakage. The pattern material comprises substantially spherical particles within the particle size range of about 10 microns to about 70 microns particle diameter, the use of which reduces the number of random, localized surface depressions and pits to improve pattern surface texture and uniformity. Patterns so formed inpart the same improvements to the surface of subsequent investment cast components. The resulting castings exbibit improved as-cast surface finish and reduced random, localized surface pitting, thereby reducing or eliminating expensive post casting surface finishing operations. Moreover, the spherical morphology of the filler particulates reduces injection pressures to fill a pattern die cavity as compared to non-spherical filler particulates. The lower injection pressures eliminate or reduce breakage of ceramic cores positioned in the die cavity for manufacture of hollow cast components, such as internally cooled turbine blades and vanes.
In an investment casting method wherein a mold is formed about disposable pattern of a component to be cast, the pattern is removed, and molten metal is cast into the mold to form a cast component, the improvement comprising forming the mold about a disposable pattern having generally spherical filler particulates having particle sizes effective to provide an improved, uniform pattern surface texture characterized by substantially reduced random, localized surface depressions and pits, said improved, uniform pattern surface being imparted to the component cast in said mold made using said pattern.
In an investment casting method wherein a pattern of the component to be cast is formed by injecting pattern material about a ceramic core, a mold is formed about the pattern including the ceramic core therein, the pattern is removed, leaving the core in the mold, and molten metal is cast into the mold about the core, a method for improving as-cast surface finish of the cast component and reducing core breakage or cracking comprising forming the pattern from pattern material having generally spherical filler particulates within the particle size range of about 10 microns to about 70 microns particle diameter effective to provide an improved, uniform pattern surface texture characterized by substantially reduced random, localized surface depressions and pits, said improved, uniform pattern surface being imparted to the component cast in said mold made using said pattern.
Pattern material for use in forming a pattern for forming an investment casting mold, comprising a meltable matrix constituent and substantially spherical filler particulates within the particle size range of about 10 microns to about 70 microns particle diameter effective to provide an improved, uniform pattern surface texture characterized by substantially reduced random, localized surface depressions and pits, said improved, uniform pattern surface being imparted to the component cast in said mold made using said pattern.
A method of making substantially spherical particulates comprising phenolic resin material, comprising heating said material to a liquid and atomizing the liquid to form substantially spherical particles.
Dependencies are inferred from the claim text.