Hydrogenated polymer

Abstract

A hydrogenated polymer obtained by hydrogenating a conjugated diene polymer having an average vinyl bond content of 20% by weight or more and less than 40% by weight to a degree such that 85% or more of double bond residues in the conjugated diene unit portion are hydrogenated, wherein (1) the crystallizing peak temperature and the hydrogenated vinyl bond content satisfy the formula: −2.8V+100<T<−2.8V+130 wherein T is the crystallizing peak temperature (° C.) measured by DSC; and V is the hydrogenated vinyl bond content (%), (2) the molecular weight is 60,000 to 600,000, and (3) the molecular weight distribution is 1.55 to 5.0. The hydrogenated polymer is excellent in mechanical strength, heat resistance, weatherability and processability and, when blended with other thermoplastic resins or rubbery polymers, provides molded articles with well-balanced physical properties such as impact resistance and moldability.