Triple-phase nano-composite steels
AssigneeMMFX Technologies Corporation
InventorsGrzegorz J. Kusinski, David Pollack, Gareth Thomas
Life of this patent
Estimating the term…
Abstract
Carbon steels of high performance are disclosed that contain a three-phase microstructure consisting of grains of ferrite fused with grains that contain dislocated lath structures in which laths of martensite alternate with thin films of austenite. The microstructure can be formed by a unique method of austenization followed by multi-phase cooling in a manner that avoids bainite and pearlite formation and precipitation at phase interfaces. The desired microstructure can be obtained by casting, heat treatment, on-line rolling, forging, and other common metallurgical processing procedures, and yields superior combinations of mechanical and corrosion properties.
Claims22
An alloy carbon steel comprising iron and a maximum of 0.35% by weight of carbon, said alloy carbon steel having a triple-phase microstructure comprising ferrite crystals fused with martensite-austenite crystals, said martensite-austenite crystals comprising laths of martensite alternating with thin films of austenite.
A process for manufacturing a high-strength, corrosion-resistant tough alloy carbon steel, said process comprising:
- (a) forming an alloy composition comprising iron and at least one alloying element comprising a maximum of about 0.35% by weight of carbon in proportions selected to provide said alloy composition with a martensite transition range having a martensite start temperature of at least about 300° C.;
- (b) heating said alloy composition to a temperature sufficiently high to cause austenitization thereof, under conditions causing said alloy composition to assume a homogeneous austenite phase with all alloying elements in solution;
- (c) cooling said homogeneous austenite phase sufficiently to transform a portion of said austenite phase to ferrite crystals, thereby forming a two-phase microstructure comprising ferrite crystals fused with austenite crystals;
- and
- (d) cooling said two-phase microstructure through said martensite transition range under conditions causing conversion of said austenite crystals to a microstructure containing laths of martensite alternating with films of retained austenite.
Dependencies are inferred from the claim text.