Controlled release urea-formaldehyde liquid fertilizer resins
AssigneeGeorgia-Pacific Resins, Inc.
InventorKurt D. Gabrielson
Life of this patent
Estimating the term…
Abstract
A controlled release urea-formaldehyde liquid resin having a nitrogen level of at least 28 wt % and its method of manufacture. The controlled release urea-formaldehyde resin is useful as a fertilizer.
Claims18
A urea-formaldehyde liquid resin prepared by a method comprising:
- 1) combining formaldehyde, urea, and ammonia in a basic solution at a formaldehyde/urea/ammonia ratio of about 0.6-1/1/0.25-0.35;
- 2) heating the solution to about 80° C. to about 95° C., and holding while maintaining pH of at least 7 for at least 45 minutes;
- and
- 3) cooling the solution to less than about 50° C., and adjusting the pH to about 9.5 to about 10.5;
- wherein the nitrogen content of the urea-formaldehyde resin is at least about 28 wt % based on 100% resin solids and about 50 wt % to about 60 wt % of the nitrogen is controlled release and about 40 wt % to about 50 wt % of the nitrogen is quick release.
2 more elements
A method of producing a urea-formaldehyde liquid resin comprising:
- 1) combining formaldehyde, urea, and ammonia in a basic solution at a formaldehyde/urea/ammonia ratio of about 0.6-1/1/0.25-0.35;
- 2) heating the solution to about 80° C. to about 95° C., and holding while maintaining pH of at least 7 for at least 45 minutes;
- and
- 30 cooling the solution to less than about 50° C., and adjusting the pH to about 9.5 to about 10.5;
- wherein the nitrogen content of the urea-formaldehyde resin is at least about 28 wt % based on 100% resin solids and about 50 wt % to about 60 wt % of the nitrogen is controlled release and about 40 wt % to about 50 wt % of the nitrogen is quick release.
2 more elements