Burnish resistant powder coating composition
AssigneeReichhold, Inc.
InventorsEric Dumain, Alan Toman, Goro Iwamura
Life of this patent
Estimating the term…
Abstract
The present invention provides a low gloss powder coating composition comprising a polyester having hydroxyl and carboxyl groups and glycidyl-containing acrylic copolymer, the copolymer having a Tg less than about 55° C. and a number average molecular weight greater than about 8000.
Claims39
A burnish resistant powder coating composition comprising:
- (a) a polyester resin having hydroxyl and carboxyl groups, and having a Tg less than about 55°;
- and
- (b) a glycidyl-containing acrylic copolymer, the copolymer having a number average molecular weight greater than about 8000.
A burnish resistant powder coating composition comprising:
- (a) about 20 to 95 percent by weight polyester resin having hydroxyl and carboxyl groups and having a Tg less than about 55° C.;
- (b) about 5 to 60 percent by weight a glycidyl-containing acrylic copolymer, the copolymer having a number average molecular weight greater than about 8000;
- and
- (c) about 2 to 20 percent by weight of a blocked isocyanate derivative.
A method for the preparation of a burnish resistant coating on an article of manufacture, the method comprising applying to the article a powder coating composition comprising a polyester resin having hydroxyl and carboxyl groups, and having a Tg less than about 55° and a glycidyl-containing acrylic copolymer, the copolymer having a number average molecular weight greater than about 8000, and curing the coated article of manufacture at a temperature of about 120° C. to 200° C.