Process and iron-based catalyst composition for the production of syndiotactic 1,2-polybutadiene

Abstract

A catalyst composition comprising (a) an iron-containing compound, (b) a dihydrocarbyl hydrogen phosphite, and (c) an organoaluminum compound is disclosed for polymerizing 1,3-butadiene into syndiotactic 1,2-polybutadiene. The use of the catalyst composition of this disclosure avoids the use of environmentally detrimental components such as carbon disulfide and halogenated solvents. The melting temperature of the syndiotactic 1,2-polybutadiene can be varied from about 100 to about 200° C. by variations in the catalyst components and the component ratios. The ability to vary the melting temperature over such a broad range with a single catalyst composition is very desirable. The syndiotactic 1,2-polybutadiene can be used as a plastic or as an additive for rubber compositions wherein it can crosslink with conventional rubbers using conventional crosslinking agents.