A method of producing a semiconductor device having a source drain region of small junction depth

A method of producing a semiconductor device wherein, on a semiconductor substrate of a first conduction type, a silicon layer containing an impurity of a second conduction type is formed, comprising:

• the first step of successively forming a spacer layer formed from a single crystal silicon layer containing germanium and a silicon layer on the semiconductor substrate of the first conduction type;
• the second step of forming a gate oxide film of a predetermined thickness at a portion of the silicon layer formed by the first step which makes an active region;
• the third step of forming a gate electrode of a predetermined pattern on the gate oxide film formed by the second step;
• and
• the fourth step of implanting ions of an impurity of the second conduction type using the gate electrode formed by the third step as a mask for ion implantation and performing annealing in a nitrogen atmosphere of a predetermined temperature to form a source drain region in the silicon layer.

A method of producing a semiconductor device wherein, on a semiconductor substrate of a first conduction type, a silicon layer containing an impurity of a second conduction type is formed, comprising:

• the first step of successively forming, on the semiconductor substrate of the first conduction type, a buried layer of the second conduction type and a collector layer of the second conduction type;
• the second step of forming a first oxide film of a predetermined thickness on the collector layer of the second conduction type formed by the first step, implanting ions of an impurity of the second conduction type into a predetermined region in the collector layer of the second conduction type and performing annealing in a nitrogen atmosphere of a predetermined temperature to form a collector leading out diffused layer;
• the third step of removing the oxide film in a base region from within the first oxide film formed by the second step and successively forming a spacer layer formed from a single crystal silicon layer containing germanium and a silicon layer on the base region of the collector layer of the second conduction type whose surface is exposed;
• the fourth step of successively forming a polycrystalline silicon layer of the first conduction type and a second oxide film of a predetermined thickness over the entire area and patterning the polycrystalline silicon layer of the first conduction type and the second oxide film into a predetermined shape to form a base leading out electrode;
• the fifth step of forming a polycrystalline silicon layer of a predetermined thickness containing an impurity of the second conduction type over the entire area and patterning the polycrystalline silicon layer into a predetermined shape to form an emitter electrode;
• and
• the sixth step of diffusing an impurity of the first conduction type into the silicon layer to form an external base diffused layer and diffusing an impurity of the second conduction type into the silicon layer to form an emitter diffused layer in the active base layer.