Method for producing a steel part and steel part

Abstract

Method for producing a steel part comprising providing a semi-finished product made of a steel comprising, by weight: 0.35%≤C≤0.60%; 0.15%≤Si≤0.5%; 0.8%≤Mn≤2.0%; 0.0003%≤B≤0.01%; 0.003%≤Mo≤1.0%; 1.0%≤Cr≤2.0%; 0.01%≤Ti≤0.04%; 0.003%≤N≤0.01%; S≤0.015%; P≤0.015%; 0.01%≤Ni≤1.0%; 0.01%≤Nb≤0.1%; optionally 0≤Al≤0.1%; 0≤V≤0.5%; and the remainder consisting of iron and unavoidable impurities. The method further including annealing this semi-finished product at a temperature strictly lower than the Ac1 temperature of the steel; cold forming the semi-finished product into a cold formed product; subjecting the cold formed product to a heat treatment comprising heating the cold formed product to a temperature greater than or equal to the Ac3 temperature of the steel; and holding the product at a holding temperature comprised between 300° C. and 400° C. for a time comprised between 15 minutes and 2 hours.