Polyolefins compositions obtained from recycled polyolefins

A polypropylene composition comprising:

• (a) 65 to 85 weight % of a crystalline propylene polymer having an amount of isotactic pentads (mmmm), measured by 13C-MNR on the fraction insoluble in xylene at 25° C., higher than 97.0 molar % and a polydispersity index ranging from 3 to 15;
• (b) 5 to 25 weight % of an elastomeric copolymer of ethylene and propylene, wherein the copolymer having an amount of recurring units deriving from ethylene ranging from 30 to 70 weight % and being partially soluble in xylene at ambient temperature;
• wherein the polymer fraction soluble in xylene at ambient temperature having an intrinsic viscosity value ranging from 3 to 10 dl/g;
• and
• (c) 5 to 25 weight % of recycled polyethylene (r-PE) having a melt flow rate (190° C./2.16 Kg) from 0.1 to 10 g/10 min and containing an amount of polypropylene inclusions ranging from 1 to 15 weight % of the total r-PE component,
• wherein the polypropylene composition has:
• a Charpy impact resistance at 23° C. from more than 10 to 15 kJ/m2, and has a value of melt flow rate (ISO 1133 230° C./2.16 kg) ranging from higher than 3.0 g/10 min. to 15 g/10 min.;
• the percentages of (a), (b) and (c) being referred to the sum of (a), (b) and (c).