Multilayer ceramic capacitor and method for producing the same
AssigneeMurata Manufacturing Co., Ltd.
InventorShinichi Yamaguchi
Life of this patent
Estimating the term…
Abstract
A multilayer ceramic capacitor includes a multilayer body including dielectric layers, inner-electrode layers, and outer electrodes coupled to the inner-electrode layers. The multilayer body includes Ba, Ti, Ca, Mg, Zr, and R, and when the Ti content is defined as 100 parts by mole, the relative amounts are as follows: Ca, 0.03 parts by mole or more and 0.15 parts by mole or less, Mg, 0.01 parts by mole or more and 0.09 parts by mole or less, R, 2.5 parts by mole or more and 8.4 parts by mole or less; Zr, 0.05 parts by mole or more and 3.00 parts by mole or less: Si, 0.5 parts by mole or more and 4.0 parts by mole or less; and P, 0.005 parts by mole or more and 0.500 parts by mole or less. Ca is in a vicinity of the center of crystal grains contained in the dielectric layers.
Claims2
A method for producing a multilayer ceramic capacitor including a multilayer body including a stack of a plurality of dielectric layers, a plurality of inner-electrode layers in the multilayer body, alternating with the dielectric layers, and a pair of outer electrodes on a surface of the multilayer body, and electrically coupled to a portion of the inner-electrode layers exposed on the surface of the multilayer body, the method comprising:
- preparing a base powder primarily including a perovskite compound containing Ba and Ti;
- preparing a Ca compound, a Mg compound, and a compound of R as sources of minor ingredients Ca, Mg, and R, respectively;
- obtaining a mixed powder and then a ceramic slurry by mixing the base powder with the Ca compound as a source of Ca, the Mg compound as a source of Mg, and the compound of R as a source of R;
- forming dielectric layers from the ceramic slurry into dielectric sheets;
- obtaining an unfired multilayer body by stacking the dielectric sheets, a subset of the dielectric sheets including an applied electrically conductive paste for inner electrodes thereon;
- and
- obtaining the multilayer body by firing the unfired multilayer body;
- wherein the R includes at least one of Y, La, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, or Yb;
- and
- when a Ti content of the elements is defined as 100 parts by mole, relative amounts of elements are as follows:
- Ca, about 0.03 parts by mole or more and about 0.15 parts by mole or less;
- Mg, about 0.01 parts by mole or more and about 0.09 parts by mole or less;
- R, about 2.5 parts by mole or more and about 8.4 parts by mole or less;
- Zr, about 0.05 parts by mole or more and about 3.00 parts by mole or less;
- Si, about 0.5 parts by mole or more and about 4.0 parts by mole or less;
- and
- P, about 0.210 parts by mole or more and less than 0.500 parts by mole.
Dependencies are inferred from the claim text.