Steel with controlled yield ratio and manufacturing method therefor

Abstract

Disclosed are a steel with controlled steel ratio and a manufacturing method therefor. The steel comprises the following components in percentage by mass: C: 0.245-0.365%, Si: 0.10-0.80%, Mn: 0.20-2.00%, P: ≤0.015%, S: ≤0.003%, Cr: 0.20-2.50%, Mo: 0.10-0.90%, Nb: 0-0.08%, Ni: 2.30-4.20%, Cu: 0-0.30%, V: 0.01-0.13%, B: 0-0.0020%, Al: 0.01-0.06%, Ti: 0-0.05%, Ca: ≤0.004%, H: ≤0.0002%, N: ≤0.013%, O: ≤0.0020%, and the balance of Fe and inevitable impurities, wherein the components satisfy (8.57*C+1.12*Ni)≥4.8% and 1.2%≤(1.08*Mn+2.13*Cr)≤5.6%. The steel has excellent low-temperature impact toughness and aging impact toughness at −20° C. and −40° C., a rationally controlled yield ratio, and ultra-high strength, ultra-high toughness, and ultra-high plasticity, which can be used in applications such as offshore platform mooring chains, mechanical structures, and automobiles that require high strength and toughness of the steel.